安钢150t转炉溅渣护炉和底部透气
砖的维护实践
龙港，吕亚，刘磊，李艳，郭少伟，王平
（安阳钢铁股份有限公司，河南安阳455004）
摘要：对安钢150t转炉溅渣护炉和底部透气砖情况进行了介绍，溅渣护炉会对底部透气砖的使用寿命造成影响.通过对转炉工艺溅渣护炉中影响底吹的因素进行分析，进而采取相应措施，优化工艺操作，从而保证了良好的底吹透气效果，提高了转炉经济效益，
关键词：转炉工艺；溅渣护炉；复吹；透气砖
中图分类号：TF713
文献标识码：B
SpatteringLiningProtectionandMaintainanceof BtottomPororsplugin15otConverteratAgsteel
LONG Gang, LU Ya,LIU Lei, LI Yan, GUO Shao-wei, WANG Ping
( Anyang Iron & Steel Group Co. ,Lad,Anyang,Henan, 455004, P,R. China)
Abstract: The slag splashing in 150 t converter and permeable brick situation at Angsteel is introduced. The protection for the bottom of the fumace by slag splashing can affect the service life of bottom permeable bricks. Through analyzing the fac tors which may influence the bottom blowing of the process of converter protected by slag splashing, the corresponding measures and optimization of process operation were made to ensure the effect of good bottom blowing and improve the eco nomic benefit of converter operation.
Key words: converter process; spattering lining protection; compounding blow; permeable brick
0前言
顶底复合吹炼是转炉炼钢技术发展的一个重要方向，采用底吹技术可缩短冶炼时间，降低渣中氧化铁含量，提高金属收得率，降低铁合金消耗，使钢液的温度和成分均匀.另外，随着纯净钢和优质特殊钢的市场需求不断扩大，转炉复合吹炼技术已成为炼钢工艺必不可缺少的技术手段.底吹透气砖是实现转炉复合吹炼技术的核心.采用溅渣护炉以来，炉龄升高，带来的各种效益也有目共赌，但负面影响也很明显，其中最为重要的一点就是溅渣引起的底部透气砖堵塞，影响复吹效果.如何在溅渣护炉条件下，保持复吹效果是现在面临的一个重要问题，本文针对安阳钢铁股份有限公司（以下简称“安钢”）150t
收稿日期：20140623
转炉在溅渣护炉过程中出现的问题，通过采取措施使复吹效果得到明显改善进行叙述
1
溅渣护炉和复吹优点
1.1溅渣护炉优点
1)大幅度降低耐材消耗；2)大大提高转炉作业
率，达到高效增产目的；3)投资回报率高 1.2复吹优点
1)渣中含铁量降低2.5%~5.0%;2)金属收得率提高0.5%~1.5%；3)残锰提高0.02%~0.06%； 4)石灰消耗减少3~10kg/t;5）磷含量降低约0.002%；6)降低氧耗约8%；7）减少耐材消耗，提高炉龄
作者简介：龙港(1972－），男，1995年毕业于鞍山钢铁学校冶金工程专业，助理工程师