大配比澳矿的烧结试验及实践
欧超红，林钢生
（广东省韶关钢铁集团有限公司，广东韶关512123）
Sum.189 December2012
摘要：用81%的澳矿、10%的委内瑞拉矿、少量的钢渣和返矿作原料，进行烧结.结果表明配加5.5%的焦粉时，效
果最佳.烧结过程烧结收缩率较高，燃耗增加，产量提高，有害杂质少，关键调：澳矿；烧结；燃耗高；杂质少
中图分类号：TG513
文献标识码：B
SinteringtestandproductionwithlargeproportionofAustralianore
OU Chao-hong, LIN Gang-sheng
(Shaoguan Iron & Steel Group Co, Ltd. , Shaoguan 512123, Guangdong)
Abstract: A sintering test was carried out with 81%Australian ore, 10%Venezuela ore, and a small amount of steel slag plus returm ore as raw materials. The results showed that with 5. 5%coke powder added, an optimal effect was attained. By doing so, the sintering shrinkage rate was increased, fuel consumption increased, and the yield increased, while with the harmful impurities reduced.
Key words: Australian ore, sintering, enhanced fuel consumption, reduced impurity
0
前言
船级社对船体结构用钢要求越来越高，如挪威
船级社（DNV)给广东省韶关钢铁集团有限公司（以下简称“韶钢”）颁发了D级、D36级船体结构用钢板工厂认可证书.所有等级的船板中的As、Sn、Sb 元素含量应不大于0.002%.从发证时开始，所有挪威船级社船板必须达到该要求，否则不予签发产品合格证。
澳大利亚矿含As、Sn相对较低.因此，韶钢决定采用澳矿作烧结主要原材料进行工业试验，配加少量委内瑞拉矿.降低As、Sn.
1
原料条件
1.1澳大利亚矿
澳矿采用西南部的纽曼山矿，属于赤铁矿.粒度较粗.铁品位为63.6%，二氧化硅含量低，As、Sn含量很低，分别为0.008与0.002，Al,0，在2%~3% 之间.
收稿日期：20120509
1.2
委内瑞拉矿
委内瑞拉矿是比较优质的矿种之一，它的特点
是铁品位较高，脉石少，Al,O，少，有害杂质少
1.3
混匀矿粉
粒度组成见表1.混匀矿粉配比及成本见表2.
表1
混匀矿粉078.A3H粒度组成
粒度 +10 mm +8 mm +6 mm +5 mm +6目 +10目 +18日 +35目 +60目 +100日 +120目 +140目 +200目 +200目 +平均粒径
作者简介：欧超红(1956-），男，1992年毕业于广东省委党校经济管理专业，经济师。
比例 4.86 6.31 11.84 5.07 2.95 12.84 12.84 11.54 7.09 10.50 0.00 0.22 10.54 3.40
2.96
累计 4.86 11.17 23.01 28.09 31.03 43.87 56.71 68.25 75.34 85.84 85.84 86.06 96.60 100.00
te/%