KR法铁水脱硫工艺的探讨
王进文，自登涛
（广东省韶关钢铁集团有限公司，广东韶关512123）
Sum.183 December 2011
摘要：介绍了KR法铁水脱硫工艺的发展、脱硫的原理、该工艺的优、缺点及影响脱硫效果的因素，对喷吹和KR
脱硫工艺进行了比较，为铁水脱硫装置的选择提供借鉴关键词：铁水预处理；脱硫：搅择；喷吹
中图分类号：TF535.2*2
文献标识码：A
AdiscussionofKRdesulphurizationprocessformolteniron
WANG Jin-wen,BAI Deng-tao
(Shaoguan Iron & Steel Group Co., Lid., Shaoguan 512123, Guangdong）
Abstract: The principle, advantages, disadvantages and development trends of the KR desulphurization process for molten iron are briefly discussed, and the factors affecting the process described in the article, In addition, a comparison are made between the injection desulphurization process and the KR one, so as to provide a guideline for properly selecting desul phurization methods.
Key words: pretreatment of molten metal; desulphurization; KR; injection
0前言
铁水预处理已成为现代化的炼钢生产工艺：铁水预处理一复吹转炉一炉外精炼一全连铸和热装热送.当下用户对钢材质量要求越来越苛刻，一般要求钢中的硫含量控制在0.015%以下，有的其至要求达到“双零”的超低硫水平，而且考虑到减轻转炉的冶炼任务和减少转炉消耗指标，使各冶炼设备的任务更加单一化、专业化，发挥各自的特长，因此近年来国内新建转炉钢厂都配备了铁水脱硫装置，老厂则经过改造配备了脱硫装置.搅拌法作为一种主流
脱硫工艺，在国内许多钢厂得到了很好应用 1搅拌脱硫工艺
1.1搅拌脱硫工艺在国内的发展
KR搅拌法是日本新日铁广烟制铁所于1965年用于工业生产的铁水炉外脱硫技术1]，早在1976年武钢二炼钢就从日本新日铁引进了国内第一台搅拌
收稿日期：2011-05-09
法脱硫装置，单罐处理能力为70~80t，处理周期约 85min，采用CaC，基作为脱硫剂，由于当时该套装置的消耗指标及运行成本均较高，处理周期长，所以并没有在国内得到广泛推广.随着时间的推移，搅拌法脱硫工艺经过近二十年的发展，已形成为一种成熟稳定的脱硫工艺，无论消耗指标、运行成本还是处理周期都大大降低.2000年武钢二炼钢在消化了第一套搅拌法脱硫工艺的基础上，联合原武汉钢铁研究设计总院自主设计和建造了第二套搅拌脱硫装置.2001年宝钢集团一钢公司从日本川崎重工引进两套150t搅拌脱硫装置，2002年原武汉钢铁研究设计总院又在昆钢建造了两套55t的搅拌脱硫装置，2003年原上海冶金设计研究院在宝钢集团上钢三厂建造了两套40t的搅拌脱硫装置.2007年在武钢新二炼钢新建两套200t、马钢四炼钢新建两套 300t搅拌脱硫装置.韶钢新一钢工程在建两套130t 搅拌脱硫装置，这样在国内已形成了300t、200t、 150t、130t、80t、55t、40t的搅拌脱硫大、中、小系列.
作者简介：王进文（1974-），男，1997年毕业于沈阳东北大学钢铁冶金系，工程师