总第168期 2009年6月
文章编号：10099700(2009)030045~02
南方金属 SOUTHERN METALS
Sum.168 June2009
CONSTEEL电转炉工艺后喷淋冷却系统的改进
吴春明，张镇武，王恩政，杨成海
（广东省韶关钢铁集团有限公司，广东韶关512123）
摘要：Consteel电转炉工艺改造后，出现烟气SO，含量增多，道高温水汽反应后呈强烈的酸蚀性，使原喷淋冷却系
统无法正常使用；为此对喷淋冷却系统进行改进，取得了较好的使用效果，关键调：电转炉；喷淋冷却塔；酸蚀
中图分类号：X757
文献标识码：B
SuccessfulApplicationofSprayCoolingTowerInSGISsConsteelEAF
WU Chun-ming, ZHANG Zhen-wu, WANG En-zheng, YANG Cheng-hai(Shaoguan Iron&Steel Group Co.,Ltd.,Shaoguan 512123,Guangdong)
Abstract : The paper introduces the function of spray cooling tower in Consteel EAF and its application after the transforma-tion of steel-making process of blending of EAF and Converter. It makes analysis and innovation of existing problem after the transformation steel-making process of blending of EAF and Converter, such as the content of SO, in the fume in-creased, and strong acid etching after reaction with steam with high temperature. Good effect was achieved. The successful application of this dedusting system of enengy-saving and environmental-friendly indictes that spraying cooling technique would have a wide room in the environmental protection technique innovation.
Key words: blending of EAF and Converter, spraying cooling tower, atomization, acid etching
0前言
广东省韶关钢铁集团有限公司（以下简称韶钢）炼轧厂的Consteel电炉是2000年12月份投产的四位一体短流程钢厂，它采用电炉在冶炼期间产生的-一次高温烟气被引人Consteel预热段内燃烧，预热废钢后进入沉降室，烟气在其内燃烧分解有害物质，并分离沉降火花等粗颗粒粉尘后进人喷淋冷却塔，经过喷淋冷却后与来自屋顶罩捕集的二次烟气相混合，满足除尘器要求的温度后，进人布袋，后由风机经烟窗排人大气，
为了降低电炉钢的成本，对Consteel电炉进行了电转炉改造：把原30%铁水+70%废钢的炉料结构的电炉工艺，改变为85%以上铁水+15%以下的废钢炉料结构的电转炉工艺.由于铁水量的增加使生产中产生的烟气量大为增加，烟气的温度也相
收稿日期：200811-05
对的高了许多同时烟气中SO，增多，遇水喷淋后显强酸性，因而对喷淋冷却塔设备及除尘管道等腐蚀厉害，对整个除尘系统的正常运行产生了很大的影响.
喷淋冷却塔的技术参数、功能 1.1功能
喷淋冷却塔内，喷枪将水与气混合直接喷人高温烟气（成雾状），水在高温烟气中蒸发完成热交换，使烟气“急剧”冷却，避免烟气中在沉降内燃烧分解的有害气体再度化合.水的喷人采取双相喷嘴，冷却水自中心孔喷出，同时压缩空气从围绕中心孔的环形间喷出，气、水压力适当，使水雾化.水量由喷淋冷却塔进出口烟气温度和流量控制，随烟气含热量变化自动进行调节.同时少量粉尘在喷淋冷却塔内沉降，定期铲车排走.见图1.
作者简介：吴春明（1971-），男，1994年毕业于湖南省袜洲冶金工业学校大专班机电一体化专业，工程师