总第189期 2012年12月
文章编号：10099700(2012)06001904
南方金属 SOUTHERNMETALS
高磁感取向硅钢涂层技术
彭志华，李智彪，刘志坚2
（1.广东盈泉钢制品有限公司，广东清远511538；2.广东省钢铁研究所，广东广州510640）
Sum.189 December2012
摘要：涂层技术在高磁感取向硅钢生产中起看重要的作用.根据生产实践，介绍了高磁感取向硅钢生产中涂层的种类和作用、涂料的成分和对产品性能的影响、涂层工艺质量控制要点和检验方法等，并提出了通过优化涂层工艺
改善高磁感取向硅钢性能和外观质量的方法关键调：高磁感；取向硅钢；涂层
中图分类号：TG132.2
文献标识码：A
Surfacecoatingofgrain-orientedsiliconsteelwithhighmagneticinductivity
PENG Zhi-hua', LI Zhi-biao'’, LIU Zhi-jian*
(1. Guangdong Yingquan Steel Products Co. , Lid. , Qingyuan 511538, Guangdong; 2. Guangdong Institute for Iron and Steel, Guangzhou 510640, Guangdong)
Abstract: Surface coating technique plays an important role in producing high magnetic inductivity grain-oriented silicon steel. Based on production practice, this paper describes the types and function of the coating, the composition of the eoat ing and its effect on the product performance, the quality control and inspection method for the coatings, as well as propoees
ways to improve the magnetic property and surface quality of the steel by optimizing the coating process. Key words: high magnetic inductivity; grain-oriented silicon steel; coating
0前言
高磁感取向硅钢具有高磁感、低铁损的优异电磁性能，主要用于制造变压器等电工产品，其性能的高低对电力电子行业的节能降耗和产品升级换代具有重要影响，是我国“十二五”期间重点发展的特种金属功能材料：高磁感取向硅钢不仅要有优良的电磁性能，而且还要求绝缘电阻高和叠装系数高、耐蚀性能和耐热性能良好、涂层附着性好、表面颜色均匀等，其质量要求和工艺难度比普通取向硅钢高.国内外正不断研究和改进涂层工艺，以进一步提高产品的性能.高磁感取向硅钢的涂层可分为隔离涂层、硅酸镁底层、绝缘涂层3种，涂层的成分和工艺与成品
的各项质量指标密切相关 1
隔离涂层 1.1简介
高磁感取向硅钢在冷轧和脱碳退火后，在送往高温罩式炉进行高温退火前，必须在钢带表面辑涂收稿日期：2012-08-23
隔离涂层并烘干. 1.2作用
1）作为退火隔离剂，防止钢卷在高温退火过程中产生粘带
2）在高温退火过程中，氧化镁和钢带表面的二氧化硅反应，生成硅酸镁玻璃膜
3）促进脱硫、脱氮反应，提高净化钢质（去除对磁性有害的夹杂物)的效果。
4）改善成品的磁性。 1.3涂料配方
取向硅钢的隔离涂层普遍以氧化镁为主，添加适量二氧化钛.在高磁感取向硅钢的隔离涂层中，还需添加少量的硼化物、硫化物、化物等添加剂，以提高玻璃膜质量和磁性.其作用为：1)二氧化钛：在高温退火过程中分解出氧，改善钢带间的气氛，氧能与钢中扩散出来的铝结合，避免铝破坏二氧化硅膜，从而保证生成良好的硅酸镁玻璃膜，提高玻璃膜的附着性，并使玻璃膜吸收氮的能力加强，同时还能提高钢带的弯曲次数，2）期化额：加强抑制能力，使二
作者简介：彭志华（1968－），男，1990年毕业于华南理工大学化工机械专业，工程师