总第211期 2016年8月
文章编号：10099700(2016)04=001604
南方金属 SOUTHERNMETALS
Sum.211 August2016
0345E热轧圆钢冲击性能不合格原因分析
李祥龙，雷中钰，陈远生，董凤奎
（宝钢集团广东韶关钢铁有限公司，广东韶关512123）
摘要：运用金相显微镜、扫描电镜对冲击不合格的Q345E热轧圆钢进行了分析和研究.结果表明，成分偏析、马氏体条带是导致圆钢冲击性能不合格的主要原因.降低夹杂物含量、减轻偏析和优化轧制工艺可提高冲击性能合格率
关键词：Q345E；圆钢；低温冲击
中图分类号：TG113.26*2
文献标识码：A
CauseAnalysisofUnqualifiedImpactProperties
ofHotRolledRoundSteelQ345E
LI Xiang-long, LEI Zhong-yu, CHEN Yuan-sheng, DONC Feng-kui
(Baosteel Group Guangdong Shaoguan Iron and Steel Co. , Ltd. , Shaoguan, Guangdong, 512123, P. R., China)
Abstract : The hot rolled round steel Q345E which the impact test was not qualified is analyzed and studied by means of met-allographic microscope and scanning electron microscopy (SEM). The results show that the composition segregation and Mar-tensite stripe are the main factors causing the non-compliance of impact performance. The qualified rate of impact resistance
o aeoeas aaoo aa r Key words: Q345E; round steel;low-temperature impact
0前言
低合金高强度结构钢，广泛用于国民经济建设各部门，例如石油管线、石油平台、桥梁、大型建筑物的建设和船舶、车辆、机械设备等的制造.最近某厂在进行力学性能检验时，发现某批次的Q345E热轧圆钢一组-40℃冲击中有一个试样冲击值异常偏低，不满足标准要求.利用金相显微镜、扫描电镜等对这组Q345E冲击试样进行成分、断口形貌、夹杂、组织等分析，找出了造成Q345E低温冲击性能异常
的主要原因. 1
试验材料及方法 1.1试验材料
材料是D75mm的Q345E低合金热轧合金结构圆钢，在同一根钢材上四分之一直径处沿纵向取3 收稿日期：2016-02-22
个试样，按GB/T229-2007《金属材料夏比摆锤冲击试验方法》在-40℃进行冲击试验.结果按一组 3个试样的算术平均值进行计算，允许其中有1个试验值低于规定值，但不应低于规定值的70%.试样冲击性能与化学成分见表1、表2.
表1Q345E钢-40℃的冲击吸收能量
试样号冲击吸收能/J
1号 100.9
2号 101.5
3号 19.9
标准 ≥34
从表1可以看出同一批次的3个试样在同样的试验条件下，冲击吸收能量差别非常大.表2中1 号、2号、3号试样的化学成分符合CB/T14292-1993《碳素结构钢和低合金结构钢热轧条钢技术条件》.将冲击合格试样与冲击不合格试样成分进行对比分析，两者成分并没有明显差异，说明化学成分不是冲击性能不合格的主要因素，
作者简介：李祥龙（1988－），男，2012年毕业于太原科技大学材料物理专业，助理工程师，