主盐浓度对化学镀 Ni-Fe-P合金性能的影响
姚柳洁，陈艳芳，刘典科，孙凯乐，王亚龙
（河南科技大学材料学院，河南洛阳471003）
摘要：研究了镀液中主盐浓度对铜基体化学镀的影响，通过测定镀速、硬度、镀层形貌、自腐蚀电位，以确定主盐的最佳使用浓度，结果表明当主盐的浓度为25g/L时，镀速、耐腐蚀性、硬度适宜，镀层分布均匀、紧凑、颗粒细小关键词：主盐；Ni-Fe-P；键速；硬度；耐腐蚀性
中图分类号：TG146
文献标识码：A
ImpactofMainSaltonPerformanceofElectrolessofNi-Fe-Palloy
YAO Liu jie, CHEN Yan fang, LIU Dian ke, SUN Kai le, WANG Ya long
(School of Materials, Henan University of Science & Technology, Luoyang, Henan, 471003, P. R. China)
Abstract: The influence of the main salt concentration in plating solution on the chemical composite coating of copper sur-face is studied. In this paper, the best concentration of the main salt is confirmed by testing the plating speed, hardness and coating morphology and self corrosion potential. Results show when the concentration of the main salt is at 25g/L rate, the planting rate is of the highest, the copper surface has a proper hardness coating and the best coosion resistance, The distribution of plating on the surface is even, compact and of fine grain.
Key words; main salt; Ni Fe P; plating speed; coating microstructure; hardness; corrosion resistance
铜及铜合金材料具有较为优良的导电、导热性
能，故广泛应用于电子、电工材料领域，值在高温下容易与氧气发生反应生成铜和氧化铜的易熔共晶，从而致使材料产生裂纹，并且由于吸氢而产生气孔，这此都不利于耐高温、耐腐蚀等现代工业对材料的性能要求().在Ni-Fe-P化学镀液中对铜基体实施化学镀以得到Ni-Fe-P复合镀层，可以在保持铜基体良好的导电、导热的前提下提高材料的耐磨、耐腐蚀以及耐高温等性能，可大大延长工件的使用寿命，从而具有更广阔的使用空间[2]，本文主要研究主盐浓度对镀速、镀层硬度、形貌、耐腐蚀性的影响，得出主盐的最佳浓度
实验方法 1
1.1实验材料及化学药品
基体为纯铜，尺寸为35mm×15mm×0.4mm；收稿日期：2013-11-29
主盐为硫酸镍；还原剂为磷酸二氢钠；其它为：氢氧
化钠，磷酸钠，硫酸亚铁，柠檬酸钠，乙酸钠等， 1.2实验仪器及设备
JSM-5610LV型扫描电子显微镜、AUTO-LAB128N型电化学工作站、MH-3型数显显微硬度计、DZKW-D-2型电热恒温水浴锅、H198107笔式酸度计、101A-2型电热鼓风恒温干燥箱、电磁搅拌器等.实验装置，见图1.
搅拌器
样品
烧杯
恒溢水浴锅
图1化学镀装置
基金项目：河南科技大学青年科学基全(2012QN042)；河南科技大学大学生训练计划(2012038）作者简介：姚柳洁（1992-），女，河南科技大学材料学院冶金专业在读。