第31卷第6期 2010年12月
·工艺研究·
热处理技术与装备
RECHULI JISHU YU ZHUANGBEI 渗碳保护试验
沈伟毅，李昭昆，邹燕珍，袁新（洛阳LYC轴承有限公司，河南洛阳471039）
Vol. 31,No.6 Dee,2010
摘要：渗碳保护试验（防渗碳涂料、镀铜、焊接试验）表明防渗碳涂料可以起到较好的保护渗碳作用，能达到对某重点轴承套图的两端面起渗碳保护作用，使套图的两端面硬度不高以保证渗碳热处理后冷加工工序能进行钻孔等加工，减少了端面留量，满足了用户的要求并又为公司创造了经济效益。关键词：防渗碳涂料；轴承
中图分类号：TG156.8*1文献标识码：B
文章编号：1673-4971(2010)06-0030-03
CarburizingTestinProtective
SHENWei-yi.LIZhao-kun,ZHOUYan-zhen,YUANXin(LuoyangLYCBearing Co.，Ltd.，LuoyangHenan471039，China）
Abstract: The test of protection for carburizing (coating for protective carburizing, copper plating, weld-ing test) shows that carburizing protective coating may play the beter protection carburizing. After using this coating,there is the play the cementation protective function to some key bearing ring's two end sur-faces, This process ensures a lower carburized hardness on two ends of the ring after carburizing,so that can meet boring processing need and reduce the end allowance for rings and satisfy user's requirements,
and has also created a great economic benefits for the company. Key words : coating for protective carburizing; bearing
某重点轴承目前为公司最大的渗碳钢制轴承且结构、加工工序复杂，渗碳热处理后电于硬化层深，这就给后加工工序钻孔等加工带来了加工难度（硬度较高），很难加工，为此开展该重点轴承的攻关试验，即渗碳保护方法试验（防渗碳涂料、镀铜、焊接试验），以期达到车加工端面留量减少，对轴承套圈的两端面起渗碳保护作用，使套圈的两端面硬度不高，保证渗碳热处理后，能进行钻孔等加工，满足了用户
的要求并又为公司创造了经济效益。 1试验试样
取与某重点轴承套圈同材料的20Cr2Ni4A钢 d300棒料截取一段作为做镀铜试验的试样，见图1，收稿日期：2010-08-27
防渗碳涂料试验的试样见图2。取与某重点轴承套圈同材料的20Cr2Ni4A钢d55棒料截取两段做焊接试验的试样，见图3。
钢层一
图1镀铜试样
Fig.1Sample af oopper-plating
作者简介：沈伟毅（1963－），女，高级工程师，主要从事轴承的热处理技术工作。
联系电话：13526964702;Email;lyswy8@163.com