合金元素总含量与碳含量之比对高铬铸铁萍火工艺的影响
吴邦富
（安徽省经济发展促进中心，安徽合肥230031）
摘要：研究了高铬铸铁的Cr、Mo、W、V等碳化物形成元素的总含量与碳含量的比值（K值）对其萍火工艺
的影响。结果表明，高铬铸铁的K值越大，其火温度应越高，保温时间也应越长，这样才能使硬度达到技术要求。K值相近的高铬铸铁，其火工艺也相近。根据K值调整泽火工艺，可提高高铬铸铁件的质量。
关键词：萍火：高铬铸铁；合金元素总含量；含碳量
中图分类号：TG164
文献标识码：A
文章编号：1008-1690(2016)02-0018-03
EffectoftheRatioofTotalAlloyingElementsContenttoCarbonContent
onHardeningPracticeofHighChromiumCastIron
WUBangfu
(Economic Development Incitation Centre of Anhui Province,Hefei 230031,Anhui China)
Abstract: The ratio of total content of carbide forming elements such as Cr, Mo, W, and V to carbon content, i. e. K value, on hardening process of a high chromium cast iron was investigated. The results indicate that as the K value of the high chromium cast iron becomes larger its austenitizing temperature should be higher, and time at the temperature should be longer, to conform the hardness to the requirement. If the K value of high chromium cast irons are similar, so too do their hardening practices. The quality of high chromium cast iron part may be improved by adjusting hardening practice as per the K value.
Key words: hardening; high chromium cast iron; total alloying element content; carbon content
高铬铸铁因其性价比高而得到了广泛应用。为进一步提高硬度、改善其组织与性能，以提高材料的耐磨性和使用寿命，往往在熔炼时复合加人碳化物形成元素（Mo、W、V、Nb、Ti)中的一种或几种，并对
其进行相应的热处理“")。 1试验材料和方法
现生产一种耐磨环，外径60mm，内径30mm，高度20mm。材料为高铬铸铁，在熔炼时复合加人 Mo、W、V等元素.其化学成分范围如表1所示。本
文使用M7型直读光谱仪进行材料化学成分分析，使用高频红外碳硫仪和分光光度计对C、S、P进行测定，使用MM6型金相显微镜进行显微组织观察。在HR-150A洛氏硬度计上测试材料硬度。铸件退火后进行粗车、半精车，然后淬火、回火，回火后硬度为62～65HRC。再精加工，尺寸达到公差范围
(0~0.005mm)。 2工艺试验
多元合金高铬铸铁则由于其化学成分的复杂性
表1高铬铸铁耐磨环的化学成分（质量分数，%）
Chemical composition of the wear resistant ring of high chromium cast iron(mass fraction, %)
Table1
C
si
Mn
P
s
Cr
Mo
W
V
0'0~0'00'0~0500~00'1L~0
10000080090000000000
收稿日期：2015-10-20
作者简介：吴邦富（1945-），男，安徽合肥人，硕士，高级工程师，主要从事金属材料及热处理技术、科研工作。
曾任中国机械工程学会热处理分会会员、安徽省热处理学会常务理事。联系电话：13965082438E-mail：wuxiyan26@sohu.com
· 18 万方数据
《热处理》
2016年第31卷
第2期