第36卷第5期 2015年10月
热处理技术与装备
RECHULIJISHUYUZHUANGBE
Vol.36,No.5 Oet,2015
·表面改性技术与工艺，
超声波对铝合金微弧氧化陶瓷层的影响
部雅楠，沈德久
（燕山大学材料科学与工程学院，河北秦皇岛066004）
摘要：文章采用铝合金作为基体材料，利用自制的WH-1A型微弧氧化设备进行表面处理。针对微弧氧化中后期陶瓷层质量差、生长速率低等问题，引入了超声波。结果表明：超声波的加入可提高陶瓷层的生长速率并促进中后期陶瓷的继续生长；使陶瓷层与基体结合处到表面的硬度变大，并且
有利于α-Al,O，的生成,提高陶瓷质量；超声波震荡作用使表面更加光滑平整。关键词：微弧氧化；铝合金；超声波；相组成
中图分类号：TG146.2*1文献标志码：A
文章编号：1673-4971（2015)05-0037-04
InfluenceofUltrasoniconMicro-arcOxidation
CeramicLayerofAluminiumAlloy
GAO Ya-nan, SHEN De-jiu
(School of Materials Science and Engineering, Yanshan University,Qinhuandao Hebei 066004 , China) Abstract: In this article, surface treatment of aluminum alloy as the matrix material is conducted by home made WH-1A type of micro-arc oxidation equipment. Ultrasonic ware is introduced to solve the poor quali ty of the micro-arc oxidation ceramic layer and low growth rate in the middle and later periods. Results show that the addition of ultrasonic wave can improve the growth rate of the ceramic layer and promote it continue growing in the middle and later periods. Uitrasonic wave make hardness from juncture of the ce ramic layer with substrate to surface increase,and is advantageous to generate α-Al, O,, and improve the quality of ceramic.Ultrasonic oscillations make the surface more smooth and flat.
Key words:micro-arc oxidation; aluminum alloy; ultrasonic wave; phase composition
等离子体电解氧化（简称PEO)或称微弧氧化是一种新颖的等离子体增强化学-电化学-烧结等物理化学冶金综合过程，可在铝、镁、钛等阀金属及其合金表面原位反应生长出与基体结合牢固的氧化物陶瓷层，从而有效改善被处理表面的耐磨性和耐蚀性等[1-3]。微弧氧化工艺中后期陶瓷层生长质量差、速率低等问题，已成为制约该技术快速发展的难题(4-6]。本课题拟引人超声波振动诱发微缺陷的方法，提高微弧氧化中后期陶瓷层生长速率、质量与能
收稿目期：2015-05-26
效。超声波额率高，方向性强，穿透本领大，尤其是在液体中能产生空化现象等特点，并且由于声波是疏密波，更易于沿着无缺陷或缺陷少的区域传播。因此超声波在高击穿阻抗区内充分发挥诱发微缺陷的作用，促使陶瓷层生长质量更高，速度更快[7-9]。
实验材料、设备和方法 1
实验所用原料为6061铝合金。微弧氧化所需的试样不需要活化、酸洗等复杂的前期处理过程，主