第36卷第3期 2015年6月
热处理技术与装备
RECHULIJISHUYUZHUANCBEI
Vol.36,No.3 Jun,2015
·设备·
冷轧带钢退火原理及连退炉内露点测量与控制
邢巍，戚新军
（安钢集团冷轧有限责任公司，河南安阳455000）
摘要：结合安钢集团冷轧分公司生产的连退炉机组实例，分析了带钢退火原理，同时对连退炉露点进行论述，并积极总结经验，对连退炉内露点的测量与控制提出方法和措施。经过一段时间的试运行，取得了一定的效果，有效控制了连退炉内露点的分布量，提高了带钢表面质量和退火后的机械性能。
关键调：冷轧；带钢；连退炉；露点
中图分类号：TG155.1*4文献标志码：A文章编号：1673-4971(2015)03-0045-03
Annealing Principle of Cold Strip and Measurement and Control
ofDewPointinContinuousAnnealingFurance
XING Wei, QI Xin-jun
(Anyang Iron and Steel Group Cold rolling Co., Ltd., Anyang Henan 455000, China)
Abstract: The principle of strip annealing is analyzed with the examples of continuous annealing fumace unit produced by Anyang Iron and Steel Group Cold Rolling Branch, the dew point of continuous annealing furnace is discussed, the experience is actively summarized, and the methods and measures for measure-ment and control of dew point in continuous annealing furnace are put forward. After a period of trial oper ation, we have obtained certain effect and effectively controlled distribution of dew point in continuous an-nealing furnace, so that the surface quality of steel strip and the mechanical properties after annealing are improved.
Keywords:cold rolling;strip steel;continuous annealing fumace;dewpoint
连续退火是连续地将带钢加热到一定温度保温后再冷却的工艺。退火目的是使热轧带钢软化、消除内应力、恢复塑性、改善带钢的金相组织]。
带钢经冷轧变形后，金属晶粒将沿着变形的方向被拉长。冷变形会引起晶粒取向的转动，从而在多晶体内形成一定类型的织构(2)。其内部组织产生大量位错，形成胞状结构，产生加工硬化，使带钢的强度和硬度大大提高，而塑性、韧性、冲压性能降低，给进一步的冷加工带来困难。金属内部组织发生晶
收稿日期：2015-03-04
粒拉长，晶粒破碎和晶体缺陷而导致金属内部自由能升高，处于不稳定状态，为了消除这种不稳定状态及所产生的缺陷，使其型性、韧性提高，强度、硬度下
降，所以需要对冷轧产品进行退火处理。 1冷轧板退火原理
形变金属的退火文称再结晶退火，是冷轧薄板生产过程中的关键工艺环节，直接影响带钢最终的产品质量。再结晶退火就是将冷变形后的金属加热