非调质钢激光表面淬火研究
谢维立1,2
Vol.34,No.2 Apr,2013
（1.上海市机械制造工艺研究所有限公司，上海200070;2.上海金属材料改性工程技术研究中心，上海200070）
摘要：使用半导体激光器对40MnSiV、48MnV、38MnVS6和12Mn2BV非调质钢试样进行激光表面淬火，分析了试样漳火后的表面硬度和显微组织。结果表明，试样表面具有很高的硬度，显微组织由
表层及心部依次是马氏体、马氏体和铁素体、床光体和铁素体。关键词：非调质钢；激光泽火；硬度；显微组织
中图分类号：TG156.33文献标志码：A
文章编号：1673-4971(2013)02-0018-03
StudyonLaserSurfaceQuenching of Non-quenchedandTemperedSteel
XIE Wei-lil2
(1. Shanghai Institute of Machine Building Technology Co. ,Lid. ,Shanghai 200070; 2.Shanghai Enginccring Research Center of Metal Materials Modification,Shanghai 200070)
Abstract: The laser surface quenching was carried out on 40MnSiV, 48MnV,38MnVS6 and 12Mn2BV non-quenched and tempered steel samples by semiconductor laser.The surface hardenss and microstruc-ture of samples after quenched were analyzed. The results indicated that there was high hardeness on sam-ple surface, and the microstructure consisted successively of martensite, martensite and ferrite, pearlite and ferrite from surface to core.
Key words : non-quenched and tempered steel ; laser quenching; hardenss; microstructure 收稿日期：2012-12-13
作者简介：谢维立（1953－），男，高级工程师，从事金属材料及热处理技术研究。
联系电话：13661489806;E-mail;13661489806@126.con
结论 4
SA33-T91钢小口径排管焊前采用火焰预热，热电偶固定方法采用点焊法，对单个焊口进行单独控温，对排管采取整体保温的方法进行热处理。升、降温速度控制在150℃/h，300℃以下不控温。SA213. T91钢排管热处理后的硬度、常温力学性能指标、金相组织均符合SA213-T91的要求。
参考文献
[1］瓦克瑞克·曼内斯曼钢管公司.T91/P91钢手册[J
0L].超（超）临界锅炉用钢及焊接技术论文集，2005
[2012-10-11 ].http://wenku.
baidu.
7c66d4282af90242a895e56b.html.
com/view/
[2]周报丰.接冶金学；金属焊接性[M]．北京：机械工万方数据
业出版社，1993
DL/T819-2002火力发电厂焊接热处理技术规程
[3]
[s].[4]
DL/T869-2004火力发电厂焊接技术规程[S]
[5][6][7]
DL/T438-2009火力发电厂金属技术监督规程[S], 美国机械工程师协会．ASMEIⅡI，2009
电力行业电力锅炉压力容器安全监督管理委员会。超（超)临界锅炉用销及焊接技术协作网第三次论坛大会论文集[C],2009.
[8］电力行业电力锅炉压力容器安全监督管理委员会．超
(超)临界锅炉用钢及焊接技术论文集[C].2005
[9][10]
杨富，章应霖，任永宁，等.新型耐热锅的焊接[M].1 饭北京：中国电力出版社，2006
雷廷权，姚忠凯.钢的形变热处理[M]，北京：中国机械出版社，1979