表面粗糙度对25Cr3MoA钢氮化层深度和组织的影响
古璟，周石桥
（中航工业南京机电液压工程研究中心，江苏南京211106）
摘要：选取25Cr3MoA钢为研究对象，采用不同的机加工方式结合干湿吹砂的方法，制备了不同表面粗趋度的25Cr3MoA钢试样。测量钢的表面粗糙度，然后对不同粗糙度的钢进行氮化处理。测量显微维氏硬度和观察氮化层，研究粗糙度对氮化层深度和组织的影响，分析产生不同差异的原因。关键词：表面粗糙度：氮化深度；显微组织
中图分类号：TG156.8*2文献标识码：A文章编号：1673-4971(2013)05-0038-02
EffectsofSurfaceRoughnessonDepthandMicrostructure
ofNitrideCaseof25Cr3MoASteel
CUJing，ZHOUShi-qiao
(Nanjing Engineering Institute of Aircraft System AVIC, Nanjing Jiangsu 211106, China)
Abstract: 25Cr3MoA steel was chosen as object of study in this paper. Different machining technologies combing with dry or wet sand blowing were used to prepare 25Cr3MoA steel sample with different surface roughness. The surface roughness of steel was tested, then steel with different surface roughness was nitri-ded. Vickers hardness was tested and the nitride case was observed. Effect of surface roughness on depth
and microstructure of nitride case were researched, and reasons of differences were analyzed. Key words: surface roughness ;depth of the nitride case;microstructure
氮化作为一种常见的化学热处理方式，可以改善钢材表面硬度和耐磨性，使之具有较好的疲劳性能而得到广泛应用。在实际生产中发现，零件表面粗糙度对氮化层深度和组织有一定的影响。本文采用机加工与吹砂相结合的方法，制备出不同粗糙度的25Cr3MoA钢试样[1,2]；25Cr3MoA钢，经调质处理后进行气体氮化，采用显微硬度法检测氮化层深度，金相法分析氮化层组织。研究不同表面粗糙度对氮
化层深度和组织的影响，分析了产生不同差异的原因，为实际生产提供依据。
1试验材料及方法 1.1试验材料
本文试验材料为航空产品常用的氮化调质钢，规格为Φ10mm的25Cr3MoA钢棒，化学成分如表 1所示。
表125Cr3MoA钢的化学成分（质量分数，%）
Table 1
元索含量
c
S
Mn
Chemical composition of 25Cr3MoA steel ( wt% )
Cr
0.20 ~0.280.10 0.350.40 ~0.70
收稿日期：2013-06-09
3.0~3.5
Mo
0.50 0.70
作者简介：古联（1984-），女，碳士研究生，主要从事冶金工艺方面的研究工作。
联系电话：15895993692;E-msil：93896748@qq.com
万方数据
P ≤0.020
s ≤0.015
Ni ≤0.30
Se ≤0.030