第35卷第2期 2015年6月
化学传感器 CHEMICALSENSORS
Vol. 35, No. 2 June.2015
LiFePO4-SDBS薄膜/锡掺杂玻璃光波导传感元件的
制备及其对有机挥发性气体的气敏性
夏依拉·吾买尔，帕提受·尼扎木丁，姑力米热·吐尔地，阿布力孜·伊米提*
（新疆大学化学与化工学院，新疆乌鲁木齐830046)
摘要：以FeSO4·7H2O、LiOH·H2O、H:PO4作为原料合成LiFePO。粉末，将十二烷基苯磺酸钠(SDBS)作为分散剂，配制LiFePO-SDBS分散溶液，利用旋转甩涂法在锡掺杂玻璃光波导表面上制备成LiFePO,-SDBS 敏感薄膜,并对其气敏性进行检测。探讨了分散剂浓度，分散时间和温度对LiFePO4-SDBS薄膜/锡掺杂玻璃
关键调：光波导气体传感器；LiFePO.-SDBS分散溶液；LiFePO4薄膜/锡掺杂玻璃光波导元件；苯乙烯：气敏性
LiFePO-SDBSthinfilm/tindopedglassopticalwaveguidesensor
and its gas sensitive properties of volatile organic gases
Xaera Umar, Patima Nizamidin, Gulmira Turdi, Abliz Yimit
(College of Chemistry and Chemical Engineering, Xinjiang University, Urumqi 830046, China)
Abstract: LiFePO4 powder was synthesized by ferrous sulfate (FeSO4 -7HO), lithium hydroxide (LiOH H,O) phosphoric acid (85%, H:PO4),twelve sodium alkyl benzene sulfonate as dispersant ,prepared the LiFePO/SDBS solution. LiFePO4 sensitive thin film was prepared on tin doped glass waveguide surface by spin coating method td detect its gas sensitivity. Experiment explores that the dispersant concentration, dispersing time and temperature have influences on LiFePO, thin film / tin doped glass optical waveguide components gas sensing properties. When ultrasonic vibration time is 2 h, the concentration of dispersant is 1%, distributed temperature is 35 °C the LiFePO. sensitive film shows good gas sensing.
Key words: optical waveguide gas sensor; LiFePO/SDBS solution; LiFePO, thin film/tin doped glass optical waveguide components ; styrene ; gassensitivity
0引言
纳米材料是20世纪80年代发展起来的一种具有全新结构的材料，它所具有的独特性质使它在磁学、光学、电学、催化以及化学传感等方面具有广阔的应用前景[1-5]。二十多年来,对纳米材料的制备、性能和应用等各方面的研究，已取得丰硕的成果[6-8]。自20世纪90年代末期以来，橄榄石型LFePO纳米材料引起广大研究者的关
基金项目：国家自然科学基金（21265020）
*通信联系人，Email;ablizyimit@xju.edu.cn，Tel:18999188174
注[9-1]，进而LiFePO。新型纳米材料迅速发展起来。由于LiFePO。薄膜具有物理化学性质稳定、便宜、无毒、不吸潮、环境兼容性好、制备工艺简单等多种优点，所以LiFePO4在纳米材料和离子传感器等方面被广泛应用【12]。很多课题组已对 LiFePO4薄膜的光学性质和气敏特性进行大量实验研究[13-15]。研究结果显示,LiFePO4薄膜具有良好的光学透明性和气敏性。为了提高敏感元件的灵敏度和改善气敏性，该研究中将十二烷基苯确