Pb-Ca合金粘状渣的组织特征
及形成机理的研究
毕晓军，许长洪，表志莉
（风帆股份有限公司有色金属分公司，河北保定071100）
摘要：铅钙系合金的熔炼过程中存在熔渣粘度大，铅、渣分高困难等同题，导致合金利用率较低。本文通过研究合金熔炼过程中合金熔渣的组成及其形成机理，找出熔渣粘稠的成国，提出粘性熔渣的控制方法，从而实现合金利用率的提高。
关键词：铅钙系合金；熔渣；粘度；铅渣；铅钙合金利用率；多元素氧化物
中图分类号：TM912.1
文献标识码：B
文章编号：1006-0847(2015)06-260-04
Studyonthemicrostructureandformationmechanism
of sticky smelting slag ofPb-Caalloy
BI Xiao-jun, XU Chang-hong, YUAN Zhi-li
(Nonferrous Metal Company, Fengfan Co.,Ltd., Baoding Hebei 0711o0, China)
Abstract: High viscosity and difficultly separating smelting slag from lead calcium alloy during the smelting process lead to low utilization rate of lead-calcium alloy. In this paper, by studying the microstructure and formation mechanism of the smelting slag, the cause of high viscosity of the smelting slag is found, and the control methods are proposed, so as to realize the improvement of utilization rate of Pb-Ca alloy
Key words: Pb-Ca alloy; smelting slag; viscosity; lead slag; utilization rate of Pb-Ca alloy; multielement oxide
0前言
用铅钙系合金制造的蓄电池具有冷起动性能好、析气量小、耐腐蚀性强、使用寿命长、无需添液维护和无污染等优良特性，因而铅钙系合金成为目前使用最广泛的板栅用铅基合金之一[1]。但是，在铅钙系合金熔炼过程中存在熔渣粘度大、铅渣分
收稿日期：2015-04-21 2602015 No.6 Vo1.52
离困难，导致合金利用率较低等问题(2)。因此研究合金熔炼过程中合金熔渣的组成及其形成机理，找
出熔渣粘稠的原因是本研究的主要内容。 1实验方法
实验材料为102号合金3，合金中@(Ca）为 0.09%~0.11%，@(Al)为0.02%~0.03%。合金材料的熔炼过程为：上炉铸锭后的熔锅中加铅升温至660～680℃，加4.5kg铝粒，同时搅拌2~3min，此时渣量不多且粘度不大，接着加铅降温，加钙约22.5kg，搅拌2～3min，此时形