CFB锅炉水冷壁的防磨措施
王万潮
（山东电力工程咨询院有限公司，济南250100）
摘要：针对某公司CFB锅炉掺烧后出现的水冷璧磨损问题，分析引发磨损的多种原固，采取针对性防磨措施，取得良好的效采，提高了锅炉运行的安全性和稳定性，对同类型的CFB 锅炉预防水冷壁磨损具有一定的参考价值。
关键词：水冷壁;CFB锅炉；磨损
中图分类号：TK223.3+1文献标志码：B文章编号：1009-3230(2013)08-0022-05 AbrasionandProtectiveMeasuresofCFBBoilerWaterWall
WANG Wan-chao
(Shandong Electric Power Engineering Consulting Institute Co., Ltd,Ji'nan 250013,China) Abstract:The paper discussed abrasion problems of water wall after a mixed buming in certain corporation's CFB boiler. A variety of abrasion reasons have been analyzed and special anti-abrasion measurements have been taken to improve the boiler's safety and stability under operation. It can be found that good results have been achieved and will provide the important reference value for the same
type of CFB boiler water wall to prevent abrasion. Key words: Bater ball; CFB boiler; Abrasion
0引言
循环流化床（CFB）燃烧技术以其优良的性能、低污染燃烧特性成为当今世界先进可靠的洁净煤技术之一，但CFD锅炉也存在一些带有普追性的问题，如：水冷壁管泄漏、耐火浇注料塌落、冷渣装置故障等，其中水冷壁管因磨损泄漏已成为制约CFD锅炉运行周期的重要因素1-1]。
某公司2009年投用了FW公司的三台FW。 465T/H-12.5紧漆型CFB锅炉，其锅炉采用水冷旋风分离器，前墙进料，床下点火，选择性风冷冷渣器；设计燃料为高硫石油焦燃料（校核燃料为焦煤重量比5：5混烧）。该锅炉投用以来一直燃用石油焦，运行工况良好。但由于煤的硬度比
收赛日期：20130618
修订日期：2013-07-10
作者简介：王万靓(1978-）男，东北电力大学热能与动力
工程专业本科毕业，山东电力工程院有限公司工程师。
万方数据
石油焦硬度高很多，势必加剧锅炉水冷壁的磨损。因此，减轻CFB锅炉内床料对水冷壁磨损，保证 CFB锅炉“安、稳、长、满、优”运行是目前急需解决的问题。
CFB锅炉水冷壁磨损机理 1
循环流化床锅炉磨损可分为冲刷磨损和撞击磨损，炉膛中心物料向上流动，近壁面处物料向下回流，当物料回流的速度方向与水冷壁管壁当地表面平行时，为冲刷磨损，此时磨损速度一般是可以接受的[3]。如果物料回流的速度方向与水冷壁管壁当地表面不平行，即存在撞击磨损。一般循环流化床锅炉床料颗粒与受热面的冲击角度为 0°~90°之间，因此循环流化床锅炉的磨损是以上两类磨损基本类型的综合结果。而水冷壁磨损主要有集中在内沿壁面回流的固体物料与炉内向上运动的固体物料运动方向相反在局部产生旋流，