流化床燃煤固硫灰渣膨胀控制因素研究
Study on Controlling Factors of Expansion of FBC Ashes
宋远明，徐惠忠，王美娥
（烟台大学环境与材料工程学院，烟台264005）
2010NO.1
摘要：分别用线性膨胀率和XRD研究固硫灰渣净浆试件的膨胀特性和固硫灰渣水化产物随龄期变化趋势，并在结合二者试验结果的基础上对膨胀控制因素进行探讨。结果显示：固硫灰渣净浆试件的线性影胀率在14~28d前增加则主要受二水石旁量所控制。
关键调：流化床；固硫灰渍；线性膨胀率；控制因素
中图分类号：TU528.041：X773
文献标识码：A
文章编号：10058249(2010)01000303
(College of Environmental and Material Engineering,Yantai University,Yantai 264005, China)
Abstract: Linear expansion ratio and X rey diffnaction (XRD) were used to study the expansion property snd the change trend by the sage of hydration products of Fluidized Bed Combustion (FBC) ashes paste respectively, followed by the investigation of the contrlling factors of expan sion., The results show that the linear expansion ratio of FBC ashes paste increases rapidly before 14 28 days, and it tums steady later. This work confims that the expansion property of FBC ashes can be divided into two phases: The linear expansion ratio of FBC ashes paste is controlled by the content of ettringite before 14 28 days, but by the content of gypsum subeequently.
Key words fluidized bed combustion; FBC ashes; linear expansion ratio; contrlling faclor
流化床燃煤固硫灰渣（以下简称固硫灰渣）是指含硫煤与固硫剂（一般为石灰石）以一定比例混合后在流化床锅炉内经850~900℃燃烧固硫后排出的固体废弃物，其中从烟道收集到的灰状物为固硫灰，炉底排出的块状物为固硫渣。
固硫灰渣除含有大量烧粘土质矿物外，还含有定量的固硫矿物（主要为游离CaO和Ⅱ-CaSO.），自身组分间即可组成火山灰反应系统。因此，固硫灰渣无需外加任何物质即具有明显的自发水硬性汀，有可能直接作为一种胶凝材料使用。目前初步研究结果表明，固硫灰渣胶凝系统极易发生膨胀，并成为制约其在建材领域应用的瓶颈问题。国内有不少建材制品生产单位不了解固硫灰渣的膨胀特性而仍参照煤粉炉粉煤灰进行使用，并经常出现制品开裂的质量事故。固硫灰渣发生膨胀的原因何在？又受哪些主要因素控制？
"基金项目：国家自然科学基金（50802082）和山东省中青年科学家奖助基金（2008BS09005）资助项目。
收稿日期：2009-1019 万方数据
解决以上问题，可帮助找到控制固硫灰渣膨胀的方法，这将极大地推进其利用进程。由于固硫灰渣出现时间相对较晚，目前未见国内外对此问题的研究报道。为此，本文在研究固硫灰渣净浆线性膨胀率的基础上，用 X射线衍射（X-raydiffraction，XRD）对固硫灰渣的膨
胀控制因素进行研究。 1试验
1.1原材料
试验用固硫灰渣的化学组成见表1。其中A~C 为固硫灰，D~E为固硫渣。灰状样品采用原状灰，渣状样品磨细过80μm方孔筛，筛余少于10%。由表1 显示，固硫灰渣含有一定量的f-CaO,SO，含量也较高。
·3·