粉煤灰综合利用
FLY ASHCOMPREHENSIVEUTILIZATION
引气剂对混凝土性能的影响研究 Effects on Properties of Concrete added with Air Entraining Agents
高辉，张雄，张永娟
（同济大学先进土木工程材料教育部重点实验室，上海201804）
NO.5
2013 专题研究
摘要：研究了引气剂对混凝土工作性、力学性能以及抗冻融性能的影响。结果表明：通过掺加引气剂增加新拌混凝土含气量，可以改善混凝土的工作性。同时混凝土的冻融耐久性得以改善，气孔间距系数越小，混土的冻融耐久性指数款越大。但是，引气剂的掺人降低了混凝土的强度，硬化混凝土平均孔径越小，越有利于减小因引气而造成的抗压强度损失。
关键调：引气剂；混凝土：抗压强度；工作性；耐久性
文献标识码：A
中图分类号：TU528.042.4
文章编号：10058249(2013)05-000703
Gao Hui, Zhang Xiong, Zhang Yongjuan
(Key Laboratory of Advanced Civil Engineering Materials of the Ministry of Education,Tongji University,Shanghai 201804,China) Abstract; Effects of air entrsining agents ( AEA) on workability, mechanical properties and freezingthawing circle of concrete were studied in this paper, The results indicated that the workability and freezingthawing circle performance of concrele added with AEA were improved; free ingthawing durability increased with the decrease of spacing factor, But .AEA decreased the compressive strength of concrete. For the hardened
wurele,the smaller the arenge pore siae is,the more wnducive to reduce the loss of compressive strength coused by AEA. Key words;air entraining agents; concrete; compressive strength; workability; durability
在20世纪30年代，美国、日本、英国等就开始使用引气剂。在美国，引气混凝土的应用已得到很大的发展。这是由于随着美国公路交通的发展，混凝土公路路面破坏严重，尤其是冬天用食盐或氯化钙溶化公路路面冰雪时，对混凝土路面破坏更为严重。应用引气剂在混凝土中引人合适的气泡（孔）是显著改善混凝土和易性与耐久性的有效技术途径[1.2]。在混凝土塑性状态引人的气泡主要影响混凝土的和易性[3，当混凝土硬化后存留的气泡则成为气孔，主要影响混凝土力学行为和耐久性(4)。由于大气孔会使硬化混凝土强度显著损失[5.6]，因此，混凝土行业对混凝土引气技术应用颜有顾虑。本文研究了引气剂对混凝土工作性、强度和抗冻融性能的影响规律，对工程实践有很强的指导意义。
（S010
国家自然科学基金资助项目（51378391)
第一作者：高辉(1981-)，女，同济大学博士研究生，主要从事建筑功能材料研究，Email：gh-online@163.com
收稿日期：2013-07-30 万方数据
1试验原材料与试验方法
原材料
1.1
水泥：安徽宁国海螺PⅡI52.5；细集料：中砂，细度模数2.54；粗集料：选用了粒径为5mm~30mm，表面比较粗糙且质地坚硬的玄武岩碎石；水：自来水；选用引气剂分别为：SJ三皂武引气剂（以A表示），烷基磺
酸盐类引气剂（以B表示）。 1.2混凝土配合比
引气剂按水泥用量的百分比（质量分数）掺加，不同引气剂掺量根据新拌混凝土的含气量调整，混凝土的落度控制在140mm~190mm，低频振动台振动15s 成型，测试新拌混凝土的含气量或成型试件用于测试硬化混凝土气孔特征参数。混凝土配合比见表1。
.7.