粉煤灰综合利用
FLY ASHCOMPREHENSIVEUTILIZATION
几种激发剂对钢矿粉活性影响的研究
2014NO.5 专题研究
Research on theEffect of different Activators of Steel Slag and Blast Furnace Slag Power
於林锋，林茂松，王琼
（上海市建筑科学研究院，上海200032）
摘要：研究了几种单一激发剂不同掺量对钢矿粉活性的激发作用及机理，优选最佳激发剂种类及掺量。结果表明：对钢矿粉激发效果较好的激发剂为半水石膏、氧化钙、二水石膏、硫酸钠、氢氧化钠，其激发剂最优掺量分别为半水石膏0.6%、氧化钙0.15%、二水石膏0.2%、硫酸钠0.15%、氢氧化钠0.03%，其中半水石膏可提高钢矿粉各龄期活性指数 8%以上。
关键调：钢矿粉；激发剂；活性指数
中图分类号：X757
文献标识码：A
文章编码：10558249(2014)05-0009-03
Yu Linfeng, Lin Maosong, Wang Qiong
Shanghai Research Institute of Building Sciences,shanghai 200032
Abstract : To obtain the optimal activator,both physical performance and mechanism on the activity of steel slag and blast fumace slag power with several single activator were investigated. The results indicated that optimal activators with the best mix proportion are 0.6% hemihydrate gypsum,0.15% calcium oxide,0.2% dihydrate gypsum,0.15% sodium sulfate and 0.03% sodium hydroxide.Especially, the activity index of steel slag and blast fumace slag power at each age was increased by 8% with hemihydrate gypsum.
Key words:steel slag and blast fumace slag power;activator;activity index
钢渣是炼钢过程中产生的副产物，产量约为粗钢产量的15%~20%"]。其化学成分与水泥熟料类似具有一定的水硬性。但由于钢渣生成温度更高，其中 C,S和C,S等活性组分结晶致密，晶粒较大，水化活性偏低，钢渣微粉单独作为掺合料的资源化利用技术尚不成熟，目前大多采用钢渣与矿渣复配钢矿粉进行生产与应用。
选用合适的激发剂对钢矿粉活性进行活化处理，可提高钢渣在钢矿粉中的掺量及产品的性能，对钢渣综合利用的规模化推广具有重要意义。已有的研究较多集中在钢渣激发剂对其活性的影响方面，而对钢矿粉复合掺合料激发剂的研究较少[2-5]。本文研究几种激发剂对钢矿粉活性的影响，为合理配制复合激发剂提供依据。
（10降二
作者简介：林茂松，男，工程师，主要从事固体废弃物资源化利用和绿色建材评价方向
收稿日期：2014-06-09 万方数据
1试验方法 1.1
原材料
(1)钢渣粉由上海海笠新型建材有限公司提供， S95矿粉由上海宝田新型建材有限公司提供，其化学组成见表1。（2)基准水泥由曲阜中联水泥有限公司提供。（3）氢氧化钠、氧化钙、半水石膏、二水石膏、硫酸钠、明矾6种市售常用激发剂由上海国药集团化学试剂有限公司提供。
表1钢渣粉、矿渣粉的主要化学成分/%
sns 钢渣41.8223.759.95
0.700.611.182.89
12.923.50
矿渣29.2744.59
14.00
1.2试验方法
0.87
7.35
0.21
0.17
0.272.34
钢渣粉与矿渣粉按3：7比例复配钢矿粉，各激发剂按一定掺量以内掺方式取代钢矿粉，参照《用于水泥和混凝土中的粒化高炉矿渣粉》（GB/T18046-2008）测定试样3d、7d、28d抗压强度，并与基准水泥对比，采
.9.