针片状含量对心墙沥青混凝土性能的影响研究 Study on the Effect of Needle Sheet Content on the Performance of Core Wall Asphalt Concrete
杨武，何建新，杨海华
（新疆农业大学水利与土木工程学院，乌鲁木齐830052）
摘要：为了得到针片状含量对心墙沥青混凝土性能的影响，分别设置了5%，15%，25%，35%，45%，55%，6 种不同针片状含量来制作沥青混凝土试件，对比其性能。结果表明：针片状含量在超过35%时，沥青混凝土性能将会大大降低，从面影响工程质量。
关键词：沥青混凝土；针片状；性能
中图分类号：TU528.42
文献标识码：A
文章编号：10058249（2017）01002003
Yang Wu,He Jianxin,Yang Haihua
( College of Water Conservancy and CivilEngineering, Xinjiang Agicultunal University,Urumqi 830052,China)
Abstract: In onder to get the effeet of needle like content on the perfomance of core wall asphalt concrete, it is set up separately5%, 15% 25%, 35%, 45%, 55%, 6 kinds af dfferent needle sheet content to make asphalt concrete specimens and compare its performance, The results
show that when the needle flake content is more than 35%, its perfomance wll be greatly reduced, thus influence the engineering quality. Keywerds: asphalt eoncrete : needle fake ; performance
在水利工程建设和施工的不断发展、安全性水平不断提高，在碾压式沥青混凝土心墙坝中，对心墙沥青混凝土的骨料要求也越来越高。在实际的试验与工程中，粗骨料对结果的影响是很显著的，也就对心墙沥青混凝土骨料的原材料性能提出了更高的要求，而目前所使用的骨料生产加工设备没有明确的规定，骨料的形状很难满足大坝建设的需求。在《土石项沥青混凝土面板和心增设计规范（SL501-2010）（11中明确规定，粗骨料中针片状含量不得大于25%，但在实际的工程中，往没有很
*基金项目：新疆维吾尔自治区高校科研计划科学研究重点项目（XJEDU2014I016）：自治区级产学研联合培养研究生项目(xjaucxyyis20141041)
第一作者：杨武（1991~），男，硕士研究生，研究方向为水利水电工程，Email;137599344@qq.com
通讯作者：何建新（1973），男，硕士，副教授，硕导，研究方向为水利水电工程，Email：xinydx_hix@126.com
收稿日期：2016-10-16·20 ·
万方数据
严格的控制这一指标。余志凯等[2}人提出在公路沥青混合料中，针片状颗粒会使沥青混合料的强度降低。张金柱等[3]人指出了在沥青混合料中，针片状含量的增加会使压碎值也随之增加，影响路面的使用寿命。在水泥混凝土中，针片状碎石增加了新择混凝土在拌合是的摩擦阻力，同时针片状碎石相比普通碎石来说坚韧性较差，从而影响了其强度特性(4) 何静等[5】人得出在公路沥青混凝土随着针片状含量的增加，最佳油石比和空隙率增大，马歌尔稳定度、动稳定度、冻融劈裂抗拉强度比和残留稳定度均降低，降低了沥青混合料的高温稳定性和水稳定性，对沥青混合料产生不利影响，建议沥青路面粗集料针片状颗粒含量不宜超过15%。宋伟等16」人提出在水泥混凝土中，针片状含量在未超过10%时，对混凝土的强度影响不大，超过10%时，混凝土的强度衰减的较明显。对于心墙沥青混凝土而言，其流动性本身相比混凝土及公路沥青混合料而言就较大，所以针片状含量对心墙沥青混凝土的影响在超过规范的要求时是否显著，或者能否超过规范的要求，我们有待