纤维增强发泡混凝土复合保温板的研究及应用
Research and Application of Fiber-reinforced Concrete Composite Foam Insulation Board
马长波，林建好
（黄淮准学院建筑工程系，驻马店463000）
摘要：介绍纤维增强水泥象苯再生颗粒发泡混凝土复合硬泡聚氨酯保温体系的材料性能、技术指标和施工方法。该技术将发泡混凝土和硬泡聚氨酯结合起来，保温和抗裂性能得到很大提高，在夏热冬冷地区的推广应用具有一定的经济效益和社会效益。
关键调：发泡混凝土；硬泡聚氨酯；外墙外保温；工程应用"
中图分类号：TU528.572;TU55*1.33
文献标识码：A
文章编号：10058249(2010)02-0039-03
( Dept, of Architectursl HuangHuai University ,Zhumadian 463000)
Abstract: The fiber-reinforoed cement polystyrene partieles recyeled concrete coreposite polyurethane foam insulation system are introduced including materisl properties, technical indicalors and construction method, which combines concrete with polyurethane fosm, thermal insulation and anti cracking performance greatly improved, and it will ffer a certain economic and social benefits with use in the summer hot and winter cold region.
Key words:foam concrete, polyurethane, exterior insulation ,engineering application
据统计，我国每年新建建筑中只有10%~15%能够达到国家标准强制性节能65%的要求，80%以上的建筑为高耗能建筑。在建筑的能耗损失中，围护结构散热损失所占的比例为40%~50%，因此围护结构在建筑节能工作中具有重要的作用。目前，围护结构的保温技术采用的是外墙外保温。外墙外保温技术一般有板类保温和涂抹类保温两种。作为板类保温技术，大多为聚苯板。而本文是以纤维增强水泥聚苯再生颗粒发泡混凝土为主材，中间复合硬泡聚氨酯做成的保温板，通过介绍其技术性能及施工方法，以扩大其在夏
热冬冷地区节能建筑中的进一步推广应用。 1
发泡混凝土复合板保温体系 1.1发泡混凝土复合板材料
纤维增强水泥聚苯再生颗粒发泡混凝土复合硬泡聚氨酯保温板是以纤维增强水泥聚苯再生颗粒发泡混凝土为主要板材，中间夹芯为硬泡聚氨酯，对于多孔砖
，基金项目：河南省科技攻关项目（2008C560002】，教科外【2008】 78号：（2010C560005）教科外[2009]987号。
收稿日期：200909-12 万方数据
体墙面，其构造如图1所示（括号内数据用于钢筋混凝土墙面）。
1.1.1发泡混凝土发泡混凝土具有密度低、保温、
隔热、隔音、隔潮等功能非常适合做为保温隔热材料，并耳生产投资少、
施工方便、可大量利用工业废渣.但其收缩大、易开裂、易吸水。为此，本板所用发泡混凝土专门加人纤维素醚、聚丙烯纤
维、可分散的有机胶粉、一益一废弃的聚苯乙烯颗粒，并
【02)(0%):
选用优质发泡剂，以改善其缺点。其生产工艺为：发泡→搅拌→混泡→成型。
硬滤家
纤维增强水决家养内生粒发泡发北板
图1保温板构造图
1.1.2硬泡聚氨酯将发泡原液A、B两组分，掺人硅粉材料，搅拌成溶剂，直接喷涂在两固定好的发泡混凝土板中间，即可立即进行系列化学反应而生成硬泡聚氨酯。其特点为：制品质轻、比强度高、导热系数低、