综合蓄热法混凝土防冻剂掺量的确定
刘方达，王维才
（中国航空港建设第九工程总队，四川成都611400）
[摘要]指出当前综合蓄热法施工中确定混凝土防冻剂接量的不尽合理之处，经试验研究提出了以混凝土热工计算公式和成熟度公式为基础，结合不同掺量防冻剂混凝土的不同冰点，提出负温混凝土防冻剂掺量的新方法。并通过试验进行了验证，得出该方法方便可行。
【关键词］混凝土；防冻剂；综合蓄热法；掺量；试验验证
【中图分类号］TU528.37
【文献标识码］A
[文章编号］1002-8498(2015)18-0009-04
DeterminationoftheAmountofConcreteAnti-freezingAgent
with Comprehensive Thermal Storage Method
Liu Fangda,Wang Weicai
(The Ninth Engineering Head Group of China Airport, Chengdu, Sichuan611400, China)
Abstract : The unreasonable aspects for ascertaining the amount of concrete anti-freezing agent used in the present comprehensive thermal storage method is pointed out. A new method for determining the amount of anti-freezing agent used in the negative temperature concrete was proposed through tests, based on the thermal calculating formula,maturity formula and the freezing points of different kinds of concrete with different amount of anti-freezing agent. The new method was proved to be convenient and feasible by tests.
Key words:concrete; anti-freezing agent; comprehensive thermal storage method;amount freezing point; testing
0引言
将混凝土的组成材料进行加热后搅拌，在经过
运输、振摄后仍具有一定温度，浇筑后的混凝土被周围保温材料严密覆盖，利用这种预加的热量和水泥的水化热量，使混凝土缓慢冷却，并在冷却过程中逐渐硬化，当混凝十温度降至0时可达到抗冻临界强度或预期强度的要求，这就是蓄热法。而综合蓄热法即在蓄热法基础上，在混凝土中掺人防冻剂，以延长硬化时间和提高抗冻害能力。防冻剂掺量的选择将会直接影响综合蓄热法的最终效果，因此混凝土防冻剂掺量的选择成为该施工方法的个关键环节。
目前混凝土防冻剂掺量的确定方法主要有如下3种：①《混凝土外加剂应用技术规范》 GB50119一2013中规定的外加剂掺量应按供货单位推荐掺量、使用要求、施工条件、混凝土原材料等因
【作者简介】刘方达，助理工程师，E-mail330204257@qq-con［收稿日期］2015-03-11
9
素通过试验确定[1-2]，但确定混凝土防冻剂所需掺量的时间太长不能及时指导施工；②文献[3]中给出的指定负温下防冻剂的掺量公式为：a=C(1-i)W(式中：C为设计冰点防冻剂的浓度；i为计划初始含冰率；W为单位体积混凝土用水量），该公式中的许多参数不容易确定，所以使用十分不便：③文献[2]在文献[3]基础上结合经验给出的公式为： a=βKT(W/C)（式中:β为参数，与水泥品种有关；K 为防冻剂掺量系数；T为环境负温度；W/C为水灰比）。该公式易于操作，但未考虑其他外加剂对防冻剂掺量的影响。本文通过分析混凝土的热工计算方法和成熟度计算理论，提出了一种新的防冻剂
掺量的确定方法，并进行了试验验证。 1理论分析
《建筑工程冬期施工规程》JGJ/T104一2011中有混凝土的蓄热法计算方法包括混凝土蓄热养护开始到任一时刻的温度计算和混凝土蓄热养护开始到任一时刻的平均温度计算及混凝土蓄热养护