2017年3月下第46卷第6期
D0I:10.7672/sgjs2017060065
施工技术
CONSTRUCTIONTECHNOLOGY
纳米CaCO，对混凝土抗硫酸盐腐蚀性能的影响*
张茂花，何佳
（东北林业大学土木工程学院，黑龙江哈尔滨150040）
【摘要】将纳米CaCO，加人混凝土中进行混凝土抗硫酸盐腐蚀试验，研究纳米CaCO，掺量对混凝土抗硫酸盐腐蚀性能的影响。试验结果表明：掺加缩米CaCO，可以提高混凝土的抗硫酸盐腐蚀力，且纳米CaCO，掺量为1%时，改善效果最明显。
【关键调】混凝土；纳米CaCO,:抗硫酸盐腐蚀；试验
【中图分类号］TU528
[文献标识码】A
[文章编号】1002-8498(2017)06-0065-04
EffectofNano-CaCO,ontheSulfateCorrosionResistanceofConcrete
ZhangMaohua，HeJia
(School of Civil Engineering, Northeast Forestry Unisersity, Harbin, Heilongjiang150040, China)
Abstract: Nano-CaCO, was added into the concrete and the sulfate corrosion resistance test was conducted. Then the influence of the amount of Nano-CaCO, on the sulfate corrosion resistance of concrete is studied. The test results show that the incorporation of Nano-CaCO, can improve the sulfate corrosion resistance of concrete, and the improvement effect was the most obvious when the content of Nano-CaCO,was1%.
Key words:concrete;Nano-CaCO,; sulfate corrosion resistance; tests
0
随着现代工业化的快速发展，一些城市的场地土、地下水被严重污染，被腐蚀性介质污染后的场地土、地下水与基础混凝土形成全浸泡、半浸泡、干湿交替循环的密切接触与作用环境，复杂的地下环境破坏混凝土基础，影响混凝土基础的耐久性0)。由于建筑基础属于隐蔽工程，其腐蚀现象不易被发现，发现后治理起来则远比上部结构困难，腐蚀破坏后果也往往是难以修复的、毁灭性的。其中，硫酸盐腐蚀是造成混凝土基础破坏的主要因素之一。因此，提高混凝土基础的抗硫酸盐腐蚀性能是至关重要的。
随着科技的发展，采用新技术和新材料是提高混凝土耐久性的必经之路。纳米材料是一个新兴的材料科学领域，由于其颗粒小、比表面积大，从而具有表面效应、界面效应、尺寸效应、量子效应等传统材料不具有的特征(23)。已有研究表明，将适量的纳米材料添加到混凝土中，可以有效地改善混凝
。中央高校基本科研业务费专项基金资助项目（2013CBQ02）：黑龙江省博士后科研启动金项目（LBH-Q13001）
【作者简介】张茂花，副教授，E-mail：zmh7716@163.com
[收稿日期】2016-08-03；【修订日期】2016-11-13 万方数据
土的微观结构，提高混凝土的耐久性。
65
本文将纳米CaCO，加人混凝土中，通过对混凝土进行抗硫酸盐腐蚀试验，研究纳米CaCO，掺量的变化对混凝土抗硫酸盐腐蚀性能的影响，并进行机理分析。
1试验概况 1.1试验材料
1)水泥选用P·042.5级普通硅酸盐水泥，其主要化学组成为：21.36%SiOz，5.16%Al,0，， 3. 94% Fe,O,,62.09% Ca0,1. 82% MgO,2. 51% S0,, 烧失量1.58。3，28d抗压强度30.5，67MPa,3,28d 抗折强度4.9，7.5MPa，比表面积320m/kg。
4选用河砂，细度模数为2.40，属
2)细骨料中砂。
3)粗骨料选用粒径为5~31.5mm连续级配的玄武岩碎石。
4)纳米材料选用纳米CaCO,，主要技术指标为：白色粉末，平均粒径30nm，纯度99%，干燥失重 0.2%.pH值9.3。
5)减水剂选用FDN型奈系高效减水剂，其外观为棕色粉末，主要成分为β萘磺酸甲醛缩合物。