66
DOI:10. 7672/sgjs2015030066
施工技术
CONSTRUCTION TECHNOLOGY
2015年2月上第44卷第3期
粉煤灰掺量对钢筋与混凝土黏结性能的影响
张晓慧
（中铁十八局集团第一工程有限公司，河北涿州072750）
[摘要]采用架式试验对粉煤灰混凝土的薪结性能进行研究。试验结果表明：掺加适量的粉煤灰能够有效提高钢筋与粉煤灰混凝土的黏结强度，随着粉煤灰掺量的增加，加载端钢筋应变变大，黏结破坏所需要的外加荷载也越
大，钢筋与粉煤灰混凝土的黏结性能也显著提高。【关键词］混凝土；粉煤灰；黏结性能；应力
［中图分类号］TU317.1
【文献标识码］A
[文章编号】1002-8498(2015)03-0066-04
InfluenceofFlyAshContentontheBondPerformance
of Reinforced Concrete
Zhang Xiaohui
(The First Engineering Co. , Lrd. of China Raileay 18th Bureau Group
Co., Lid.,Zhuozhou, Hebei 072750, China)
Abstract:The beam test is used to research the bond performance of fly ash concrete.The test results indicate that the bond performance of steel bars and concrete can be improved by adding fly ash in concrete specimens.The more fly ash added in, the more strain of steel bars increased, so as the external load for bond failure.As a result the bond performance of steel bars and fly ash concrete was improved obviously
Key words : concrete; fly ash; bond performance; stress
0引言
钢筋与混凝土之间的黏结作用由3部分组成，分别为化学胶着力、摩擦力以及机械咬合力。因此，良好的黏结性能是钢筋混凝土结构承受荷载作用的前提。黏结的退化和失效将导致钢筋混凝土结构力学性能的降低和破坏。所以钢筋混凝土的黏结性能一直是工程研究中的一个重要课题，钢筋与混凝土的黏结滑移关系始繁是研究的一大难点[2-3]。粉煤灰是目前工程中应用最为广泛的混凝土掺和料，中国水泥市场上几乎所有水泥都掺有粉煤灰。众所周知，粉煤灰的掺人对混凝土的力学性能和耐久性都有一定的影响，关于这方面的研究已经很深入[4]。但粉煤灰对混凝土与钢筋黏结性能的研究却不多，极少的部分研究采用的都是中心拉拔或者轴拉试验[56]，考虑钢筋混凝土在实际工作中的受力状态较为复杂，各部分的受力状态不同，仅通过中心拉拨试验和轴拉试验无法真实反应钢
【作者简介］张晓慧，工程师，E-mail：463420563@qq-com[收稿日期】2014-09-16
筋与混凝土之间的相互作用。本文通过与构件实际受力状态相似的梁式试验来研究钢筋与混凝土
的黏结问题。 1试验
1.1试件设计
梁式方法本身包含的变量多，试验复杂。为了简化试验，仅从粉煤灰混凝土的粉煤灰掺入量方面进行试验研究，研究不同掺量的粉煤灰对钢筋混凝土黏结性能的影响。试验中混凝土强度等级为 C40，粉煤灰掺量为10%，15%，20%，25%。实际工程中螺纹钢筋用量最大，故本文采用螺纹钢筋制作试件。
参考RILEM-CEB-FIP建议的梁式黏结试验，进行梁式试件的结构设计[7]。试验梁的几何尺寸为 150mm×240mm×1260mm。钢筋采用HRB335直径为16mm，取10d为有效黏结长度（d为测试钢筋的直径），在试件的黏结区内开槽粘贴钢筋应变片，并用PVC管套筒隔离黏结区以外的钢筋。为了测试自由端钢筋滑移量和跨中的挠度，分别在试件两