拉脱法检测混凝土抗压强度试验研究
朱跃武，邱平，游启洪
（中国建筑科学研究院建研科技股份有限公司，北京100013）
2013年12月下第42卷
第24期
【摘要】简要介绍了拉脱法检测混凝土抗压强度技术的原理、特点和已完成的试验和验证工作过程，采用夹紧、拉脱、数据采集为一体的拉脱仪，利用自动调节径向夹紧力的特点，完成对芯样试件的拉脱试验。拉脱法检测混凝土
抗压强度技术被列为2013年度住房和城乡建设部规范编制计划。【关键词】混凝土；拉脱法；拉脱仪；检测
【中图分类号】TU317
【文献标识码】A
[文章编号】1002-8498(2013)24-0078-04
ExperimentalStudyofConcreteCompressive
StrengthbyPull-offTest Zhu Yuewu, Qiu Ping,You Qihong
(CABR Technology Co., Lad. ,China Academy of Building Research,Beijing100013,China)
Abstract:This paper describes the principle and characteristics of inspection of concrete compressive strength by pull-off test, and the process of testing and validation are also introduced. The technology uses clamping, pull-off, gathering data as one of the pull-off device, and the automatic adjustment of the radial clamping force is used to pull-off the core samples. Inspection of concrete compressive strength by pull-off test was listed as 2013 annual specification preparation of the plan of the Ministry of Housing and Urban-rural Development.
Key words : concrete; pull-off test; pull-off equipment; inspection
已有检测技术的比较 1
1.1微破损检测技术的特点
混凝土强度检测技术广泛应用于混凝土施工质量控制、验收、鉴定、评估等方面。目前，我国常用的混凝土强度检测技术分为无损检测和微破损检测。无损检测主要有回弹法、综合法、超声法等；微破损检测主要有钻芯法、拔出法、后锚固法、直拔法等。无损检测操作方便，但检测结果误差较大。微破损检测结果虽精度较高，但存在工序多、操作不便等缺点，如常用的钻芯法因芯样直径粗，对结构损伤大，在钻取、切割、磨平、抗压等环节中易出现偏差，会影响实测强度值。研究更加简单、方便的微破损检测技术具有重要意义，拉脱法就是在这种需求情况下被研究开发出来的，拉脱法和已有微破损检测技术的特点如下。
1)钻芯法试件制作过程：在结构上钻取，2012年住房和城乡建设部科技计划项目（20121902420730023）[作者简介】朱跃武，高级工程师，E-mail;bw9817@163.com
【收稿日期】2013-08-11 万方数据
Φ100mm的芯样；切割成高径比1:1的芯样试件；对两个承压面进行打磨。试件在压力机上进行试压，可以检测C10~C100的混凝土抗压强度。缺点为不适合钢筋密集部位；对结构损伤大；试件加工繁项，宜出现误差。
2)后装拔出法试件制作过程：在结构上钻孔：打磨扩孔：安装膨胀螺栓。试验方法为采用拔出仪将膨胀螺栓拨出，采集拨出时的拉力峰值。仅可以检测混凝土强度≤C50的混凝土。缺点为操作工艺较复杂：操作时间长：拨出装置较难完成高强混凝土的检测。
3)后锚固法试件制作过程：在结构上钻孔；清孔；插人锚栓；灌人环氧树脂；养护。试验方法为采用拔出仪将锚栓拨出，采集拔出时的拉力峰值。仅可以检测混凝土强度≤C80的混凝土构件，缺点为拔出装置功率大、体积重，操作工艺较复杂；采用环氧树脂胶结拔出试件宜对环境造成污染；受温度影响大，操作时间长。
4）直拨法试件制作过程：在结构上钻制小芯