第40卷第9期 2010年9月
涂料工业
PAINT&COATINGSINDUSTRY
氧化锌对氯化橡胶防污涂料性能的影响姜蓬勃，黄洁，张松，刘宏宇（九二一一七部队，北京100072）
Vol.40No.9 Sep.2010
摘要：研制了添加不同含量氧化锌的氧化橡胶防污涂料。通过考察防污涂料的稳定性、机械性能和防污性能，综合分析了氧化锌对氯化橡胶防污涂料性能的影响。研究结果表明：氧化锌的添加量在7%~9%范围内能有效地抑制由铜离子引发的交联反应，能够保证氧化橡胶防污涂料的稳定性。
关键词：氯化橡胶：防污涂料；氧化亚钢；氧化锌；稳定性
中图分类号：TQ637.2文献标识码：A文章编号：0253-4312（2010)09-0058-03
EffectofZincOxideonPropertiesof Chlorinated
RubberBased Antifouling Coatings Jiang Pengho,Huang Jie,Zhang Song,Liu Hongyu
(The92117UnitofPLA;Beijing100072,China）
Abstract: Several samples of chlorinated rubber based antifouling coatings with different content of zinc oxide have been prepared.The effect of zinc oxide on the properties of chlorinated rubber based antifouling coatings has been systematically analyzed by investigation of the stability, the mechanical properties and the antifouling performance of chlorinated rubber based antifouling coatings.It has been shown that zinc oxide can effectively inhibit crosslink reaction aroused by copper ions, and ensure the stability of chlorinated rub-ber based antifouling coatings when its content is in the range of 7%~9%.
Key Words: chlorinated rubber; antifouling coatings; zinc oxide; cuprous oxide; stability
0引言
海洋生物对船体及其他海洋设施的附着污损会带来一系列严重间题，如降低船舶行驶速度、增加油耗、破坏水下结构和阻塞水下管线等。防污涂料能有效抑制海洋浮游生物对舰船及海洋设施的污损腐蚀"。由于Cu,O具有低毒、广谱、对环境危害较小的特点[2]，因此以氧化亚铜为主要防污剂的氧化橡胶涂料仍是目前应用最广泛的防污涂料之一。
然面，氯化橡胶防污涂料贮存稳定性相对较差，长时间存放会因氧化、交联等因素而影响涂料的机械性能及防污性能。本研究旨在通过研究氯化橡胶防污涂料的稳定性，考察影响涂料稳定性的因素，从而为此类涂料的配方设计提供参考依据。
1实验 1.1原材料
树脂：氯化橡胶、氧化石蜡、松香、丙烯酸改性树脂（CM-1)等。颜颠填料：氧化亚铜、氧化铁红、氧化锌等。其他助剂：润湿分散剂、偶联剂、防沉剂、防污助剂。有机溶剂：二甲苯、乙
作者简介：姜蓬勃（1970一），男，工程师，主要从事防房蚀涂科研究。 58
酸丁酯等。
1.2配方设计及制备工艺
将松香、氟化石蜡、丙烯酸树脂按比例完全溶于有机溶剂中，然后加氯化橡胶高速分散溶解。依次加人颜填料和助剂，研磨搅拌分散均匀。配方见表1。
表1防污涂料基本配方
Table 1The basic formula of antifouling coatings
组分
氯化橡胶松香
氯化石蜡 CM-1 氧化亚铜氧化锌偶联剂防沉剂防污助剂其他颜填料混合溶剂
te/% 6~10 8~12 3~5 6~10 22~30 0~12 0.5~1.5 0.5~1.5 5-15 5 25~30