第42卷第5期 2012年5月
涂料工业
PAINT & COATINGS INDUSTRY
涂料中可溶性Pb、Cr含量测定结果误差原因分析
张大亮，徐鹏，孟飞燕，管淑玉，张自端
（国家建筑装修材料质量监肾检验中心，郑州450004）
Vol.42No.5 May2012
摘要：研究并详细讨论了涂料样品制备与样品前处理过程中，各个因素对可溶性Pb、Cr含量测定结果的影响。结果表明：漆膜的厚度、粒径、提取液的酸度、温度等因素对结果的测定有较大的影响，应当对这些因素予以控制以提高实验室间结果一致性。
关键调：涂料；可溶性重金属；检测；结果误差
中图分类号：TQ630.7*2
文献标识码：A
文章编号：02534312(2012)05006104
CausalAnalysisofResultant Errors in Determinationof SolublePbCrinPaint
Zhang Daliang, Xu Peng, Meng Feiyan, Guan Shuyu, Zhang Ziduan
( National Center for Quality Superuision and Inspection of Building Decoration Materials, Zhengzhou 450004, China)
Abstract: The various factors that influence the determination result of soluble Pb, Cr in paint during the paint film preparation and pretreatment of samples were investigated and discussed in details. The result in-dicated that the film thickness, powder size, pH of HCl extraction solution and temperature showed dramat-ically influence on the result. It was recommended that these factors should be controled to improve the result consistency in different laboratory.
Key Words: paint; soluble heavy metals; determination; resultaut errors
可溶性重金属含量的测定不同于总含量测定，后者能得到准确的结果，而前者的测定结果受样品制备、样品处理以及测试过程中各种因素影响较大。国标检测方法GB/T18581-2009《室内装饰装修材料溶剂型木器涂料中有害物质限量》（重金属检测项目按GB/T18582—2008《室内装饰装修材料内增涂料中有害物质限量》附录D)以及相关标准En71=3玩具安全-第3部分：特定元索的迁移、ASTMF963-11玩具安全标准消费者安全规范、IS08124-3玩具安全-第3部分：特定元素的迁移及GB/T6675—2003国家玩具安全技术规范等也均未对样品制备、处理以及测试条件进行明确规定，造成了实验室间对标准理解的差异。目前我国有关实验室间涂料中可溶性重金属检测结果的一致性很差(1-2)
本文以醇酸调和漆为研究对象，详细考察了样品制备与样品前处理过程中各因索对可溶性Pb、Cr含量测定的影响与规律。为提高实验室间溶剂型木器涂料中可溶性重金属含量测定结果的一致性提供参考。
【基金项目】质检公益性行业科研专项项目（编号：200910063）
1
实验部分
1.1
仪器与试剂
原子吸收光谱仪（AA6300）：岛津（中国)有限公司；铅、铬空心阴极灯：岛津（中国）有限公司；pHs-3C型酸度计：上海华侨仪表厂；HJ-1型磁力加热搅拌器：江苏省金坛市荣华仪器厂；电子天平：BT224S,Sartorins；不锈钢金属筛：上虞市大地分样筛厂；铅、铬、标准储备液：国家标准物质研究中心；盐酸（HCI）溶液：分析纯，浓度37%，密度1.18g/cm"，开封化工二厂；实验样晶：醇酸涂料样品由郑州市双塔涂料有限公司提供。
仪器工作条件
1.2
Pb测定条件是测量波长：283.3nm；灯电流：10mA；空气/乙炔=15/2.0；单色器狭缝宽度：0.7nm。Cr测定条件是测量波长：357.9nm；灯电流：10mA；空气/乙炔=15/2.8；单色器狭缝宽度：0.7nm。
作者简介：张大亮(1961一），男，高级工程师，主要从事涂料的质检与科研工作。
61