应用研究
第42卷第10期 2012年10月
涂料工业
PAINT & COATINGS INDUSTRY
阻燃型弹性丙烯酸饰面涂料的研制
陈铁鑫，郭岳峰（北京东方雨虹防水技术股份有限公司，北京101309）
Vol. 42No. 10 Oct.2012
摘要：采用紫外光固化的弹性丙烯酸树脂为基料,改性聚磷酸铵为阻燃剂，制备了聚氮酯泡沫用阻燃型弹性丙烯酸饰面途料，通过正交试验对涂料配方进行了优化，确定了阻燃剂最佳含量为35%。考察了紫外光和太阳光对涂层拉伸强度的影响，紫外光4h，太阻光7d，途层拉伸性能达到最佳：采用氧指数及质量损失评估了涂层的阻燃性能
关键词：阻燃：弹性：饰面涂料；丙烯酸
中图分类号：TO637.6
文献标识码：A
文章编号：0253-4312(2012)10005805
Developmentof Fire-Retardant Elastic AcrylicFinishing Coating
Chen Tiexin, Guo Yuefeng
(Bejing Oriental Yuhong Waterproof Technology Company, Bejing 101309, China)
Abstract: The fire retardant elastic acrylic finishing coating applied on polyurethane foam was prepared with UV eurable elastomeric acrylic emulsion as binder and modified ammonium polyphosphate(APP) as fire retardant,Orthogonal test was used to optimize the coating formulation,the best content of fire retardant was 35%. Effection of UV and sun lights on coating tensile property were studied, and found that exoposure to UV 4 h and sun light 7 d, the tensile strength reached the highest; coating fire - retardant property was ev-alated by use of oxygen index and mass loss.
Key Words:fire resistance;elastic;finishing coating;acrylic
硬质聚氨酯泡沫(PUF)是一种具有保温隔热和一定防水功能的新型合成高分子材料，其具有良好的保温、隔热功能导热系数为0.022W/（m·K），非常有利于建筑节能，且不透水、不吸湿、绝缘、吸音、耐油、耐化学腐蚀。目前，随着我国建筑节能事业的发展，被建筑业称为“新时代保温材料“的聚氨酯已开始在建筑节能领域展露其优越的性能和良好的发展潜
氢酯泡沫耐候性及耐紫外线性能差，因此不能
真接
膜，防止
丙烯酸乳液为
通常是在聚氨酯泡沫外表面涂覆一层保护
清润深著化。
本研究采用可紫外光固化的弹性
其料，以改性多聚磷酸铵为阻燃剂，制备了阻燃
型弹性丙烯酸饰面涂料，考察了紫外光及太阳光对涂层拉伸
，同时运用氧指数及质量损失方法考察了途层阻
性能的影响，
燃性能，通过与国外某产品进行比较，本产品达到国外的先进技术水平。
1实验
1.1实验仪器及试剂
CMT5504微机控制电子万能试验机；ATLASUV2000紫外老化箱：ATLAS-Ci4000氙灯老化箱：JF-3氧指数测定仪： SF04高速砂磨搅拌机;STM-IV斯托默黏度计：LX-C部氏
硬度计：JA2003A电子天平。
弹性丙烯酸乳液：国外产品；金红石型二氧化钛：龙螺钛业：普通聚磷酸铵、改性聚磷酸铵（APP）、季戊四醇（PER）、三聚氰胺（MEL）：杭州捷尔思：重钙、高岭土、滑石粉等、助剂：均为市售。
1.2实验方法
实验基本配方见表1，涂料制备流程如图1所示。
表1实验基本配方 Table 1Basic test recipe
组分乳液阻燃剂二氧化钛填料水
各种助剂
e/% 30 ~40 10~30 5~5 2~5 10~20 适量
按图1将一定量去离子水及各种助剂加人到研磨机的搅拌罐中预分散，然后加人填料、阻燃剂，高速搅拌得到浆料。向浆料中加人乳液及增稠剂，在电动搅拌机作用下低速搅拌，过滤后得到阻燃型弹性丙烯酸饰面涂料。
作者荫介：陈铁鑫（1981一），男，硕士，研究方向：水性饰面防火涂料及钢结构防火涂料。 58