红外隐身涂层及对雷达吸波性能的影响
邢孟达"
赵宏杰
林海燕
宫元勋
(1航天特种材料及工艺技术研究所，北京100074）（2中国人民解放军驻二一八厂代表室，北京100001）
邓国卫2
文摘研究了红外雷达兼容隐身涂层红外发射率及雷达波隐身兼容性的影响因素，包括填料的类型、质量分数及涂层厚度。研究表明，以填充30wt%的HW-3型铝粉为填料，制备的涂层厚度为20um时，涂层红外发射率达到0.25，能大幅降低材料表明红外辐射温度，且对微波隐身兼容性良好。
关键词红外隐身，微波兼容，涂层
中图分类号：TQ433.4+3
DOI:10. 3969/j. issn. 10072330. 2015. 04. 012
Infrared Stealth Coatings and Its Impact on Radar Absorbing
XING Mengda'
DENGGuowei?
ZHAO Hongjie'
LIN Haiyan'
GONG Yuanxun'
(1Research Institute of Aerospace Special Materials and Processing Technology,Beijing100074)(2Representative Ofice of People's Liberation Ammy Stationed at 218 Factory,Beijing 10001)
AbstractWe have investigated three significant factors affecting emissivity and microwave compatibility of infra-red stealth coatings, including type of infrared stealth filler, content and thickness of the coating. It is found that the coating with 30wt% HW3 aluminum powder as infrared stealth filler and thickness of 20 μm has the lowest infrared emissivity of 0. 25. In addition, it can effectively reduce the surface temperature of infrared radiation and remain superi-or compatibility of microwave absorbance.
Key wordsInfrared stealth,Microwave compatibility, Coating
0引言
为了实现微波、红外一体化隐身，需要在微波吸收材料表面再涂覆一层红外隐身涂层，尽可能降低军用飞机的红外辐射强度，同时兼容微波隐身。目前美国在微波、红外兼容隐身材料的研究上处于领先地位，如 F-117、F-22战斗机,不仅可以在宽带范围内实现微波隐身，而且可以使飞机表面的红外辐射下降60%~ 70%。其他国家如俄罗斯、英国等也大力发展红外隐身涂层在飞行器上的应用，如俄罗斯的图-160海盗旗、英国的海鹰隐身导弹、法国的幻影2000战斗机、目本的SX-3隐身反舰导弹等[1-4]。
本文选用了3种不同类型的红外隐身颜料，对比分析了它们的红外发射率特性及微波隐身兼容性。
1实验 1.1材料
HW-1型铝粉（杆状，粒径为60μm）、HW-2型铝收稿日期：20150420
粉（杆状及片状，25wm）、HW-3型铝粉（片状，10 m）、丙烯酸聚氨酯清漆、吸波底板。吸波底板是由掺混吸收剂的环氧树脂与玻璃布复合，通过模压工艺或
热压罐工艺制备得到。 1.2设备
电子天平（万泰WT60001X）、高速搅拌器（谷澡 JB-12KD）、烧杯等；喷涂设备包括高压气泵（GSX100）、吸上式喷枪（岩田W-101-152S）、喷涂平台、气砂（豪瑞斯SHD-216)等；测试设备包括涂-4杯（精鼎JD-507）、红外发射率测量仪（IR-2型）、RAM 反射率弓形法测试平台、热红外成像仪（FLIR
SC7000)。 1.3过程
(1)对吸波底板进行均匀打磨，然后用原子灰刮补平板表面气孔。
(2)将红外隐身颜料及丙烯酸聚氨酯清漆按照一