第43卷第8期 2015年8月
聚氢乙烯 Polyvinyl Chloride
用手干法乙快生产的低硫电石的研制
毛晓军，秦耀伟
（河南能源豫北化工公司鹤壁电石厂，河南鹤壁458099）
【关键调】电石；干法乙炔；硫含量；兰炭；焦炭；配比
Vol.43,No.8 Aug.，2015
【摘要】分析了干法乙炔生产工艺的特点，认为GB10665—2004检测电石乙炔中硫化氢含量的方法不适用于用水量少的干法生产的乙炔，提出了新的检测方法。采用硫含量低的兰炭与普通焦炭进行合理配比，生产出了低硫电石，这种电石可用于干法乙炔的生产。
【中图分类号】TQ132.32
【文献标志码】B【文章编号】10097937(2015)08-0011-03
Development of calcium carbide with low sulfur content for dry-process acetylene production
MAOXiaojun,QIN Yaowei
(Hebi Calcium Carbide Factory, Henan Yubei Energy Chemical Company, Hebi 458099,China) Key words; calcium carbide; dry-process acetylene; sulfur content; semi-coke; coke; ratio
Abstract: The characteristics of dry-process acetylene production were analyzed. The method in GB 10665—2004 to detect the content of hydrogen sulfide in calcium carbide method acetylene was not suit able for dry-process acetylene, and a new measuring method was put forward. Low-sulfur-content semi-coke and coke were mixed in proper ratio to produce low-sulfur-content calcium carbide, and the calci-um carbide could be used in the production of dry-process acetylene.
河南能源豫北化工公司鹤壁电石厂（以下简称鹤壁电石厂）具备45万a电石产能，采用8台 30000kV·A密闭电石炉，下游产品配套10万a
1,4-丁二醇(BDO)项目。 1存在的问题
干法乙炔工艺是近些年兴起的新工艺。该工艺具有废水排放量低、废渣水含量低、转化率高等优点，电石下游产品PVC、BDO新建装置中有一部分配套采用干法乙炔技术。
河南能源豫北化工公司精细化工公司（以下简称精细化工公司）的10万VaBDO装置就采用了干法乙技术，基本全部使用鹤整电石广生产的电石。开车不久（2013年2月）发现系统中粗乙炔含 H,S体积分数高达1600×10-‘，脱硫系统不堪重负，导致后段反应硫含量超标，引起催化剂中毒。出
【收稿日期】201410-11
现问题后，对余下的电石按照国家标准取样分析，发现电石中硫含量极低，属于优级品。产品质量和用户使用出现了矛盾，鹤煤电石厂迅速组织相关人员
进行研究攻关，于2014年3月解决了这个难题。 2原因分析
2.1国家标准中H,S含量分析的局限性
现行电石国家标准为GB10665—2004，经过研究，发现该标准乙炔生成方式属于湿法乙炔工艺，其加水量远高于干法乙炔的理论用量，因而其适用于湿法乙炔工艺是毋庸置疑的。但是笔者发现，按照这种方法得到的数据与精细化工公司乙炔实际H,S 含量（色谱检验）存在非常大的差异。两种方法检验数据对比见表1。
从表1可见：按照国家标准检验，H,S含量是合格的，但在精细化工公司BDO装置乙炔生产系统
【作者简介】毛晓军（1968一），男，本科，高级工程师，1991年毕业于河南农业大学土化专业，长期在氯减行业工作，曾
在聚氯乙烯》(中国氯碱》发表论文多篇，现任河南能源豫北化工公司鹤壁电石厂化验室主任。
11
万方数据