第38卷第12期
2010年12月【助剂】
聚氯乙烯
Polyvinyl Chloride
Vol.38,No.12 Dec.，2010
提高汞资源循环利用率促进氯碱行业持续发展
李国栋，周军
（新璧天业（集团）有限公司化工研究院，新疆石河子832000）
[关键词］PVC；氧化汞催化剂；无汞催化剂；汞资源回收：循环利用率
[摘要］结合电石法PVC行业乘资源的利用现状及无乘催化剂研究进展，提出降低求消耗的现实思路及途径，有序推进行业求减排。
[【中图分类号］TQ325.3，TQ426
[文献标志码]A
[文章编号］10097937(2010)12002704
Raising the utilization rate of mercury resources to promote sustainable development of chlor-alkali industry
LIGuodong，ZHOUJun
(Chemical Rescarch Institute of Xinjiang Tianye (Group) Co., Ltd., Shihezi 832000, China) Key words: PVC; mercury chloride catalyst; mercury frcc catalyst; utilization of mercury re
sources; circulation utilization rate
Abstract: Based on current utilization situation of mercury resources in carbide based PVC in-dustry and the rescarch progress in mercury free catalysts, rcalistic thoughts and methods for rcduc-ing mercury discharged consumption were proposed, in order to advance the reduction of discharged mercury in PVC industry orderly.
Foundation item: Supported by National Key Technology R&D Program(2008BAB41B00)
汞是一种稀缺资源重金属，供应量逐年减少。 2008年，国内PVC产量为881.7万({)，其中电石法PVC实际产量占到75%2)。电石法PVC生产过程中，需要使用以活性炭为载体的氟化汞催化剂（氟化汞质量分数10%～12%），生产1tPVC氯化汞催化剂消耗量为1.0～1.2kg。粗略估计，当前国内每年消耗氟化汞催化剂约8000t.折合汞资源消耗已经达到500t，占国内汞资源消耗总的 50%，超过全球汞消耗量的15%。降低汞消耗和污染是关系到PVC行业发展的迫切任务，也是实现 PVC行业可持续健康发展的关键环节。
从汞削减的角度来看，国内外都着眼于“逐步削减，直至完全停止汞的使用”。当前解决电石法
［收稿日期］2010-03-16
［基金项目］国家科技支撑计划（2008BAB41B00）
PVC行业汞消耗过大的困局，也基本延续了这种思路。首先要采取切实可行的措施来逐步降低汞消耗，同时加大无秉催化剂的开发力度，最终实现电石法PVC行业的无汞化。笔者重点从催化剂的角度来谈谈实电石法PVC行业汞减排的可行性。
1提高汞资源的循环利用率是当前汞减排的关键
1.1PVC行业汞资源的利用现状
电石法PVC行业汞资源的使用与消耗涉及3 个环节：①氯化汞催化剂的生产制备，②氯化汞催化剂的使用，③汞资源回收与冶炼。目前，受管理和技
【作者简介李国栋（1977一)，男，工程师，目前任新亟天业（集团)有限公司化工研究院催化剂课题组组长，负责氯乙
烯合成催化剂的研发工作。