聚氯乙烯
Polyvinyl Chloride
超高分子质量聚氟乙烯树脂的研制
刘松涛“，余文骊，张月芳
（上海氯碱化工股份有限公司，上海200241）
关键词］聚氯乙烯；超高分子质量；扩链剂；聚合度；凝胶率
Vol.41, No.9 Sep.,2013
「摘要］介绍了平均聚合度为4000的超高分子质量聚氯乙烯树脂的合成工艺，讨论了扩链剂流加时间及用量、聚合温度、分散剂种类等对产品性能的影响，确定了小试工艺配方并进行了稳定性试验，
［中图分类号］TQ325.3［文献标志码］B［文章编号］1009—7937(2013>09—0005—05
Preparation of PvC resinswith ultrahighmolecular weight
LIU Songtao,SEWenli,ZHANGYuefang
(Shanghai ChlorAlkali Chemical Industry Co ., Ltd ., Shanghai 200241, China)
Key words : PVC; ultrahigh molecular weight ; chain extender ; polymerization degree ; gel content Abstract : A synthesis process of PvC resins with ultrahigh molecular weight , i .e. average pol-
ymerization degree 4 o00, was introduced. The effects of chain extender feeding time and amount , polymerization temperature , dispersant type on the properties of products were disscused . The small experiment process formula was determined , and the repeatability test was carried out .
超高分子质量聚氯乙烯(PVC)树脂是指平均聚合度≥4000的PVC树脂，是一种具有优异物理化学性能的新一代PVC树脂。用这种树脂加工的产品除保持了PVC原有的特性外，还具有压缩永久变形和热变形小、强度高、回弹性优异、消光等一般橡胶所具有的特性，因此也被称为PVC热期性弹性体,在应用中以代替橡胶为主要目的。与橡胶制品相比，其又具有加工工艺简单、成本低廉等优点，可单独使用，也可与多种弹性体或通用型PVC树脂共混改性。该树脂以软质PVC成型加工为主，可广泛应用于密封条、高强度膜材、鞋料、高温电缆等“以塑代胶”产品，具有较好的市场前景和经济效益，
本文中介绍了扩链剂CD一20用量、聚合温度、分散剂种类、引发剂种类等对合成P4000（平均聚合度为4000)超高分子质量PVC树脂的影响规律和
P4000超高分子质量PVC树脂的研制情况 1试验部分
1.1主要设备与仪器
JGF—5/40型机械密封式5L聚合釜，J—W-1*[收稿日期］2013—01—22
型微型柱塞计量泵，2XZ一1型旋片式真空泵 RB20一110型自动恒温热水泵,SS一Ⅱ型三足式离心机,BrobenderPL2000一6型转矩流变仪，Master
sizerMs20型激光粒径测试分析仪。 1.2主要原料
氯乙烯，上海氯碱化工股份有限公司；有机过氧化物引发剂，天津阿克苏诺贝尔聚合物化学品有限公司;PVA分散剂，日本、英国;HPMC分散剂，美国陶氏化学公司；扩链剂CD一20，青浦合成试剂厂。 1.3合成工艺
按照配方要求将脱盐水、分散剂、pH值调节剂等助剂依次加入5L聚合釜中：用氮气吹釜试压10 min，放掉氮气;抽真空脱氧约5min，真空度为85.3 kPa;加入1000mL氯乙烯，冷搅拌20min（搅拌速度500r/min）；加入引发剂后，10～20min升温至预定温度，聚合开始；将一定量扩链剂与水配制成溶液，聚合开始后或聚合一定时间后用计量泵流加入签内，流加若十小时：当聚合压力下降全预定压力时
[作者简介］刘松涛（1977一），男，硕士，工程师，2008年毕业于上海交通大学化学化工学院，主要从事氯乙烯聚合和新
产品开发工作。