第42卷第1期
2014年1月【科研与生产】
聚氯乙烯 Polyvinyl Chloride
氟醋糊树脂的合成试验
张月芳*，美顺芳
（上海氟碱化工股份有限公司，上海200241）
Vol.42,No.1 Jan.2014
【关键调】氯醋糊树脂；合成试验：酷酸乙烯酯；氯乙烯；共聚；豪合工艺：红外光谱
【摘要】通过氯乙烯与醋酸乙烯酶的共聚试验，研究了单体的投料配比、加料工艺、聚合转化率等对氯醋共聚糊树脂中酯酸乙烯酯含量以及树脂性能的影响规律，掌提了在10L聚合签中制备高醋酸乙烯酯含量氯醋糊树脂
的聚合工艺。
【中图分类号】TQ325.3
【文献标志码】B
【文章编号】10097937(2014)01000604
SynthesisexperimentsofVCM-VAcpasteresins
ZHANGYuefang，XI Shunfang
(Shanghai Chlor -Alkali Chemical Industry Co. , Ltd., Shanghai 200241, China)
Key words: VCM-VAc paste resin; synthetic experiment; VAc; vinyl chloride; copolymerization; polymerization process; IR spectrum
Abstract; Through the copolymerization experiments of VCM and VAc, the influence law of mon-omer feed ratio, feeding process and polymerization conversion on VAc content in VCM-VAc paste resins and on properties of VCM-VAc paste resins were studied.The polymerization process of preparing VCM-VAc paste resins with high vinyl acetate content in 10 L polymerizer was determined.
与PVC糊树脂相比，氯醋糊树脂具有较低的凝胶温度与熔融温度。一方面，酯基的引入不但增加了树脂与各种基材的黏合力，面且提高了增塑剂对树脂的落解速度，起到了内增塑作用，从而提高了流变性，改进了树脂的加工性能；另一方面，随着醋酸乙烯酯在PVC树脂上接枝率的提高，氢醋糊树脂在酮及酯类溶剂中的溶解度提高，从而拓宽了其在油
墨等领域的应用空间["]。 1试验部分
1.1主要设备与仪器
COF10/4=W型磁力耦合式10L聚合签，单层下压六叶斜浆：JW-1型柱塞计量泵；120L恒温热水槽（自控）;2XZ-4型旋片式真空泵；红外光谱仪,Spectrum One FT -IR spectrometer。
1.2主要原料
醋酸乙烯酯：71.0~73.0℃馏分的质量分数> 97%，密度0.930~0.934g/mL（20℃C)，pH值 3.5~4.5(50g/L,25C)；脱盐水：电导率≤10μS cm，pH值5~8.5；引发剂：叔丁基过氧化氢、硫酸铜（带5份结晶水）、甲醛化次硫酸钠；乳化剂：十二烷
基硫酸钠、C~混合醇。 1.3性能测定
氯醋糊树脂中醋酸乙烯酯的含量按GB/T 93472002检测。
2试验结果与讨论
氨醋糊树脂中醋酸乙烯酯的含量主要受醋酸乙烯酯投料量、聚合转化率、单体加入工艺等因素影响。随着醋酸乙烯酯投料量和转化率的提高，共案
【收稿日期】2013=01=08
【作者禽介】张月芳（1968一），女，硕士，高级工程师，2007年毕业于华东理工大学，主要从事豪氯乙烯生产及研发工
作。 6