铝合金变极性TIG焊工艺参数对焊缝成形的影响
宋宗贤
宋建岭肖宏徐岩磊（天津航天长征火箭制造有限公司，天津300462）
王雷
文摘研究了5A06铝合金变极性TIG焊接参数对焊缝成形的影响，研究表明：DCEP半波电流值增大和DCEN半率波所占比例的减小一方面会使得清理作用的宽度增大，同时也使得熔宽和熔深都有所增加；阴极清理作用一定的情况下，DCEN半波电流值越大，熔宽和熔深越大；随着频率的增加，熔宽更小，熔深更大。阴极清理作用也与频率有关系，频率越大，阴极清理作用越差。
关键词变极性，脉冲，熔深，熔宽
中图分类号：TC4
D0I:10.3969/j.issn.10072330.2014.Z1.010
PolarTechnologyParametersof TIGWeldingAluminumAlloyon
Influence of Formation of Weld
SONGZongxian
SONG Jianling
gXIAOHong
XUYanlei
WANG Lei
(ooeoneneeaoyaeuardrf)
AbstractThis paper studied the 5A06 aluminum alloy welding parameters on the weld of variable polarity TIG. Research shows that DCEP half wave current value is increased and the DCEN half wavelength of the proportion of the reduced hand will increase the width of the cleaning effect, but also makes the weld width and penetration increased. The cathode cleaning action under certain conditions,the greater DCEN half wave current value is, the greater is the weld width and penetration. The cathode cleaning action under certain conditions,the DCEN half wave current value is greater,the greater the weld width andpenetration.With the increaseofrequency,the smaller is weld width thegrea ter is the worse effect of the weld penetration. Cathode cleaning action also has a relationship with the frequency,the greater the frequency,cathode cleaning effect worse.
Key wordsVariable polarity,Pulse,Weld penetration,Weld width
0
5A06是A1-Mg系防锈铝，原牌号LF6，在不可热处理合金中强度良好，耐蚀性、可切削性良好。阳极化处理后表面美观。电弧焊性能良好。优良的抗腐蚀性能使5A06合金广泛用于海事用途如船舶，以及汽车、飞机焊接件、地铁轻轨.需严格防火的压力容器（如液体罐车、冷藏车、冷藏集装箱）、制冷装置、电视塔、钻探设备、交通运输设备、导弹零件、装甲等。采用变极性TIC焊接时，不同的工艺参数对铝合金焊缝的外观成形影响很大，同时也直接影响焊接接头的力
收稿日期：2014-07=04
学性能。本文研究了变极性TIG焊接参数对焊缝成
形的影响，从而得出最优的焊接参数。 1试验
5A06铝合金（抗拉和屈服强度分别为330和 170MPa，延伸率为22.6%）板材10mm厚， ER5356"}焊材，其化学成分见表1。采用的电源是 miller公司的变极性焊机Dynasty700，采用直线焊接工作台，氩气的保护气体流量为13~15L/min，焊接速度为150mm/min。