燃气技术GasTechnology doi:10.3969/j.issn.16715152.2012.06.003
天然气门站一起Q235B输气管线焊接事故分析
口章丘市天然气有限责任公司（250200）刘伟
摘要：本文介绍了天然气门站一起Q235B输气管线延迟裂纹事故。分析了裂纹漏检和产生原因，强调
慎用高强度级别、纤维素型下向焊进口焊条和焊完24小时后探伤检查的必要性。本文还指出：这次事故是在试验压力略高于设计压力1.5倍时发生的，当试验压力较小时，可能不会出现类似事故，但并不等予不存在延迟裂纹这一隐患，它有可能在使用中扩展，导致泄漏，希望已经投用的类似管线加强在役检验。
关键调：Q235B输气管线焊接延裂纹
AnWeldingAccidentOfTheGASTransmissionPipelineInThe
GasStation
Zhangriu National Gas Company ( 250200 ) Liu Wei
Abstract : This paper introduces an accident of the Q235 gas transmission pipeline with delayed crack. Analyses the
flaws missed in the pipelines and the cause for cracks, Emphasize be careful with high strength grades and the necessity of the check after testing 24 hours. This paper also point out that this accident happens in the test pressure slightly higher than 1.5 times the design pressure, when the test pressure is lower, this similar acciden possibly not oceur again, but not equal to that delayed crack does not exist hidden danger, it may be possible to expand in use and lead to leak. Hope to strengthen the service inspection of the similar pipeline in cast.
Keywords:Q235B
Transmission pipeline
Welding
某市××路门站管线试压，当试验压力升至6.8MPa（即设计压力的1.51倍）时，由于一个管子与弯头对接焊缝大量气体泄漏而被迫停工。
这是一条可焊性良好的低碳钢组成件形成的管线，施工队伍是颇有名气的国家级专业队伍，所有焊口都是采用进口焊条施焊的，且焊完经过了100%X射线探伤，怎么可能出现这样的问题呢？事故的原因是什么？通过这个事故，我们应该汲取哪些教训？这是
本文要叙述的。 121城市燃气·月刊
Delayed erack
1
泄漏源是焊接延迟裂纹
1.1泄漏处的位置和形状
泄漏焊缝是材质为Q235B的Φ219×8管子与20号钢Φ219×16弯头对接焊缝。泄漏处是沿焊缝弯头侧边缘（熔合线）上的开裂。具体位置和形状如图1所示。 1.2泄漏开裂的起源-—焊接延迟裂纹
经过对泄漏焊口及其相邻焊口重新进行X射线和磁粉探伤，我们又发现了一些走向沿焊缝边缘的熔合