2013年1月第44卷第1期
燃料与化工 Fuel &Chemical Processes
不黏煤混合气煤制备活性炭工艺条件研究
李亚男
（中国矿业大学化工学院，徐州221116）
35
摘要：研究了不黏煤配合气煤制备压块活性炭的工艺条件，探讨了活性炭吸附性能，实验得到最佳的工艺条件为炭化温度550℃，炭化恒温时间30min，活化温度900℃，活化时间4h。压块活性炭的碘吸附值可达1041mg/g，亚甲
基蓝吸附值为190mg/g，均符合工业生产的要求。关键调：活性炭；压块；配煤
中图分类号：TQ536
文献标识码：A
文章编号：10013709（2013）01-003503
Study on theprocess conditions of active carbonpreparation
byblending non-cakingcoal and gas coal
Li Yanan( Chemical Engineering Department, China University of Mining and Technology,Xuzhou 221116,China) Abstract: This paper studies the process conditions for preparing briquetted active carbon by non-caking coal and gas coal,and discusses the absorption property of active carbon. Experimental result shows the optimum process conditions are: coking temperature 550°C ,constant temperature time for coking 30min, activating temperature 900°C , activating time 4h. The iodine adsorptive value of briquetted active carbon is up to 1 041mg/g, and methylene blue adsorptive value up to 190mg/g.
These two values meet the requirement of industrial production. Key words: Active carbon; Briquette; Coal blending
新疆蕴藏着大量尚未开发的煤炭能源，预测资源量达219万亿t，占中国煤炭资源预测总量的 40%，位居各省首位。新疆煤种较齐全，多以中低变质的长焰煤、不黏煤和弱黏结煤为主，且品质较高，煤灰分和硫分均较低，属于优质动力和煤化工、煤制油用煤11。多年来新疆煤炭价格保持在90~110 元/，是全国平均煤价的30%~50%，属于全国的低价位能源区，发展煤化工具有明显的竞争优势【3]。
随着工业的发展，用于水处理的活性炭应用越来越多[3]。目前世界活性炭产量约70万t,其中约 50%~60%用于水处理，预计到2015年我国城市供水需煤基活性炭约15方t。工业发达国家研制的压块破碎活性炭与常规方法生产的活性炭相比，中孔数量多，亚甲兰指标高，适用于水处理等液相应用领域围]。
为弥补单种煤生产活性炭时产品性能上的缺陷，近年来研究开发了配煤生产技术。配人适当的黏结性煤，在保证活性炭具有较高的机械强度的同收稿日期：2012-09-24
作者菌介：李亚男（1988-），女，研究生万方数据
时，改善其吸附性能3]。本文利用新疆不黏煤和黏结性较好的气煤混合制备压块炭，生产吸附性能较好的活性炭，具有巨大的经济价值。
压块活性炭的制备 1.1
实验原料
本文主要采用新疆黑山原煤（XJ）和徐州矿务局气煤（XZ)混合制备压块活性炭，其工业分析及黏结指数如表1所示。
煤样的工业分析及黏结指数表1
样品 XJ xz
1.2
2.65 3.64
实验设备
工业分析/%
Vd 36.58
6.06
33.65
FC 56.86 56.65
黏结指数 0 81.7
CGJ100-3型密封式化验制样粉碎机，WE-100
型液压式万能试验机，RG-6-9型管式电阻炉，