2015年3月第46卷第2期
·煤焦技术·
燃料与化工 Fuel & Chemical Processes
一种质量特异炼焦煤的试验与研究
刘克辉",2王光辉"
（1.武汉科技大学，武汉430081；2.广东韶钢技术研究中心，韶关512123）
摘要：采用煤岩反射率检测、基氏流动度检测、单种煤炼焦试验、配煤炼焦试验等手段对A焦煤综合分析，发现A 焦煤的G值、Y值、工业分析指标等与其他同类焦煤相近甚至更好，但其显微组分异常，活情比高达19.2，最大流动
度仅32ddpm，单种煤炼焦所得焦炭的热强度低至5.26%。关键词：炼焦煤；质量；试验；研究
中图分类号：TQ533
文献标识码：A
文章编号：10013709（2015）02000903
Test and research on a kind of coking coal with abnormal quality
Liu Kehuil.2Wang Guanghui
(1. Wuhan University of Science and Technology, Wuhan 430081 ;
2. Technology Research Center of Guangdong Shaoshan Iron & Steel Co.,Lid.,Shaoguan 512123, China)
Abstract : This paper comprehensively analyzes A type coking coal with methods of coal petrography reflectance detection, Gieseler fluidity measurement, coking test with single coal and coal blending coking test etc. The test shows that The G value, Y value and industrial analysis index of A type coal are similar with and even better than other coking coal of the same kind, but its micromaceral is abnormal, and the ratio between reactive and inert components is as high as 19. 2, maximum fluidity is only 32ddpm,and the thermal intensity of the produced coke from the single coal is as low as 5. 26% . Key words: Coking coal; Quality; Test ; Research
在韶钢主要单种煤结焦性能研究项目实施过程中，发现某进口炼焦煤（以下简称A焦煤）煤质特异。其常规的煤质指标G值、Y值、工业分析指标等与其他同类焦煤相近，甚至优于其他同类焦煤，采用煤岩分析和基氏流动度检测方法分析，发现其显微组分异常，活情比高达19.26，最大流动度仅 32ddpm。通过单种煤炼焦试验、配煤炼焦试验等方法进一步检测分析，发现其热强度比其他同类焦煤显著偏低，配煤试验显示随着A焦煤配入量增加，焦炭热强度下降，配入量越大，下降越明显。
试验方法 1
采用PL2000型流动度检测仪，依据ASTM标准 D2639，对煤样进行全自动检测，分析其开始软化温收稿日期：201409-21
作者简介：刘克辉（1972-），男，高级工程师
度、最大流动度、最大流动度温度、固化温度等指标。采用蔡司显微镜、HD型煤岩及焦炭显微结构分析仪，依据GB6948一2008在反光显微镜下用油浸物镜人工测定煤光片中镜质组最大反射率、随机反射率分布、煤岩显微组分。采用WG-SJL-I型和WG-SJL-Ⅱ型甘埚焦炉，依据韶钢技术中心规程进行单种煤炼焦和配煤炼焦试验。采用北科大焦炭反应性及反应后强度试验装置，依据GBT4000一2008 检测方法分析增埚焦炉试验所得焦炭热强度。
2试验与研究 2.1常规指标分析
A焦煤及同类焦煤常规指标数据见表1。A焦煤在同类焦煤中挥发分略高，灰硫含量相对较低，黏