郑润芬：海拉尔油田贝28区块污水处理系统腐蚀控制技术
海拉尔油田贝28区块污水处理系统腐蚀控制技术那润芬
摘要：针对海拉尔油围贝28作业区含油污水处理系统管道内腐蚀严重的问题，通过现场管道挂片取得腐蚀产物，并对其进行能谱分析，同时在各取样点选取污水进行水质检测。经研究得知，该系统的腐蚀主要由硫酸盐还原菌引起。根据腐蚀原固，通过室内实验研制出兼具杀菌功能的缓蚀剂C1-1008，在德二联合站开展媛蚀剂工业性现场试验。添加缓蚀剂后，污水处理系统腐蚀速率由0.316mm/a降至0.039mm/a，缓释效率高达87.7%，有效地控制了含油污水处理系统的腐蚀问题。
关键词：海拉尔油田；污水处理；腐蚀；缓蚀剂 Doi:10.3969/j.issn.10066896.2017.2.022
Corrosion Control Methods of Wastewater Treatment System in Bei 28Block of Hailar Oilfield
Zheng Runfen
Abstract: Serious corrosion is found in wastewater treatment system since Bei 28 Block of Hailar Oilfield was commercially developed. The corrosion products were obtained by field pipeline hanging sheet, and then we carries on the energy analysis, at the same time energy analysis was carried out. Learned through the study, the corrosion of wastewater treatment system is mainly caused by Sulfate reducing bacteria. Corrosion inhibitor with bactericidal action (C11008) was developed to inhibit the corrosion of wastewater treatment system. The in-situ testing results show that C11008 had excellent corrosion inhibition efficiency. The corrosion rate of waste water drops to 0.039mm/a from 0.316mm/a with an inhibition efficiency above 87.7%.
Key words: Hailar oilfield; wastewater treatment; corrosion; corrosion inhibitor
海拉尔油田贝28作业区含油污水处理系统采用的是悬浮污泥过滤工艺（SSF)；作业区还有返排液处理站，来液为压裂返排液，同样采用悬浮污泥过滤工艺（SSF)，每年5一9月份期间运行。整个污水处理系统防腐措施仅为内置防腐涂层，建站2 年后管线开始泄漏，维修措施为焊补、小规模更换管线，3年后腐蚀程度加剧，最严重时每天都需焊补管线，给油藏注水造成了不利影响。
为研究海拉尔油田污水处理系统综合防腐措施，选取腐蚀严重并具有代表性的贝28作业区德二联合站污水处理系统为研究对象，对不同工艺段的水质进行试验和分析，确定污水系统腐蚀的主要影响因素，针对腐蚀主要影响因素开展药剂研制，经过工业化现场应用试验，开发出适合海拉尔油田污水处理系统的化学法腐蚀控制技术。
“大庆油田工程有限公司 86
万方数据
管道挂片及结果分析
1
为了准确测定污水系统处理介质的腐蚀性，需要在现场管道内进行挂片。目前常用的管道挂片法均需在管道上开孔，挂片结束后开孔位置容易泄漏，破坏管道的整体性，给生产带来不利影响，且挂片数量较少，不利于研究工作的进行。为此对管道挂片法腐蚀速率监测技术进行改进，研制出无损管道挂片实验装置！，采用在注水泵前过滤器的位置将挂片简置人管道内的方法，试片材质选择与管道相同的20"碳钢，检测污水处理系统不同时期的腐蚀情况，挂片周期为90天。
无返排液期间和有返排液期间的污水系统现场
管道挂片腐蚀形貌见图1。由图1可知，试片表面附着较厚的黑色腐蚀产物，质地疏松。有返排液时，腐蚀更为严重。
油气田地面工程http:/www.yqtdmgc.com