应用与试验
doi :10. 16576/j. cnki. 10074414. 2016. 06. 033
2016年第6期（第29卷，总第146期）·机械研究与应用·
超银焊料在铜合金压板中的工艺开发及应用
方春虎
（兰州电机股份有限公司，甘肃兰州730050）
摘要：公司从国外引进的发电机转子磁极线图压板，采用铜锋合金（黄铜)焊接结构。为了确保焊接质量，根据其焊接性能，对焊接材料、接头力学性能进行了对比试验研究，试验结果表明：转子磁极线图压板采用超银焊料，针焊焊接接头性能良好，焊接工艺可行。
关键调：超银焊料：铜合金压板；焊接工艺：力学性能
中图分类号：TG405
文献标志码：A
文章编号：1007-4414(2016)060110-02
Technique Development and Application of Super Silver Solder in Copper Alloy
FANG Chun-hu
(Lanzhou Electric Corporation, Lanzhou Gansu730050, China)
Abstract : The rotor magnetic pole coil pressure plates of generator which are imported from abroad by a company have been a-dopted the copper zinc alloy ( brass) for welding structure. In order to ensure the quality of welding, experimental comparison study of the welding material and the mechanical properties of joints are conducted according to the welding performance. The results of experiment show that the rotor coil magnetic pole plates adopt the super silver solder, and the brazing welding joints would have good performance, thus the welding process is feasible.
Key words : super silver solder; copper alloy plate; welding procedure; mechanical property
0
引言
焊接工程中经常遇到一些新材料、新结构或新的
工艺方法在批量焊接前，应进行焊接性研究工作，以确保所采用的新材料，结构或工艺方法能获得优质的焊接接头1]。某公司从国外引进发电机为四极转子，其转速较高，离心力大，自身结构强度不够，需要用铜合金压板来对结构加强。因此，为了确保铜合金压板批量生产的焊接质量，根据其焊接工艺，对铜合金压板进行了焊接工艺试验、验证，对接头综合力学性能进行了试验研究。
焊接接头力学性能试验 1
1.1焊前准备
按GB/T11363《钎焊接头强度试验方法》对接头进行力学性能试验。钎焊接头拉伸试样见图1。
S0~0自 Re
图1
60
C3.3
160
钎焊接头拉伸试样
试样采用事先加工好的试棒进行钎焊[2]。试验收稿日期：2016-11-03
共分四组，试样编号及选用焊料见表1。本试验采用氧乙炔火焰钎焊。焊接接头力学性能试验结果见表 2。焊接工艺参数如表3。
表1试样编号及选用焊料
试样编号 1#试样 2#试样 3#试样 4#试样
选用焊料
银基焊料（B-Ag45CuZn）铜磷焊料（B-Cu80AgP）
母材切条
超银焊料（FWL-1D）
表2
焊接接头力学性能试验
试样编号 1#试样
2#试样 3#试样 4#试样
1#-1 1#-2 1#3 2#-1 2#-2 2#-3 3#-1 3#-2 E-# 4#-1 4#-2 4#-3
作者简介：方春虎（1962-），男，甘肃临夏人，工程师，主要从事电机产品的焊接结构设计及焊接工艺工作。·110.万方数据
抗拉强度 R./MPa 125 115 140 248 138 160 o 0 0 125 138 138
平均值 R/MPa
126.67 182 0 133.67