焦化设备隔热层下腐蚀与防护
邱红张素君段有龙王剑刘占光
（1.中冶焦耐工程技术有限公司，大连116085；2.鞍山市技师学院，鞍山114000）
Nov.2014 Vol. 45 No.6
摘要：介绍了焦化设备隔热层下腐蚀机理，分析了其影响因素及防护措施，其中金属保护涂层是最基本的方法，并提出了隔热涂料在焦化设备的应用。
关键词：焦化设备；隔热层下腐蚀；防护；涂料
中图分类号：TQ520.5
文献标识码：B
文章编号：10013709（2014）06-003204
Corrosion under insulator of coking equipment and its protection
Qiu HongZhang Sujun’ Duan YoulongWang Jian' Liu Zhanguang
(1. ACRE Coking & Refractory Engineering Consulting Corporation,MCC,Dalian 116085,China :
2. AnShan Technician College, Anshan 114000, China)
Abstract: This paper introduces the corrosion mechanism under the insulator of coking equipment and analyzes its effect factors as well as the protective measurements,in which the metal - protective coating is the most basic measurement, and additionally proposes the application of thermal insulating coatings to the coking equipments.
Key words: Coking equipment; Corrosion under insulator; Protection; Painting
为减少设备内介质热量或冷量损失，或防止人体烫伤，维持稳定操作等，通常在焦化设备外部设置隔热结构，一般由隔热层、防潮层和保护层组成，以减少热传导。随隔热结构的推广应用，在取得节能效果的同时，产生了隔热层下腐蚀，由于对其重视程度不够和检测困难，造成物料泄漏导致的火灾和爆炸等重大安全事故，给企业造成巨大经济损失。为了更大程度地减缓隔热层下腐蚀，对其腐蚀机理、影
响因素和防护措施进行探讨是十分必要的。 1隔热层下腐蚀
1.1隔热层下腐蚀机理【1]
隔热层下腐蚀是金属与水接触产生的大气腐蚀，即金属处于表面薄层电解液下的腐蚀过程。金属表面含饱和氧的电解液膜的存在，氧的扩散比全浸状态更为容易，使大气腐蚀的电化学过程中的阴极过程由氢去极化转化为氧去极化为主（02+2H20 +4e一40H），大气腐蚀的阳极过程会受到较大阻收稿日期：2014-06-11
作者简介：邱红（1969－），女，高级工程师
滞，阳极钝化及金属离子水化过程的困难是造成阳极极化的主要原因。随金属表面电解质液膜变薄、大气腐蚀的阴极过程通常更易进行，而阳极过程变为困难。在薄液膜层下，腐蚀微电池的电阻显著增大，微电池作用范围变小，因此大气腐蚀的腐蚀形态较为均勾。
在大气腐蚀条件下，腐蚀产物的成分和结构往往很复杂。在一定条件下，腐蚀产物还会影响大气腐蚀的电极反应。Evan认为，大气腐蚀的铁锈层处在湿润条件下，可以作为强烈的氧化剂而起作用，进行下列阴极去极化反应：
6Fe00H +2e → 2Fe; 04 +2H20 +20H
即锈层内发生Fe"+、Fe+的还原反应。而当锈层干燥时，锈层中的FesO4文被由大气渗锈层的氧重新氧化为Fe3+的氧化物。由此,若在干湿交替的条件下，带有锈层的钢便能加速腐蚀。
对于奥氏体不锈钢设备，当大气环境或保温材料中含有氯化物.存在水的情况下在奥氏体不锈钢