热轧带钢表面辊印缺陷分析与改进
马啸晨，梁鹏
（唐山市德龙钢铁有限公司技术中心，河北唐山063604）
Total No.263 2017,Number11
摘要：分析了唐山市德龙钢铁有限公司热连轧带钢生产过程中表面辊印缺陷的形成原因。结合生产现状，通过优化加热温度及轧制工艺、改善轧线的冷却条件、优化生产计划缩编排、加强轧辑表面质量管理等一系列措施的落实，带钢表面辑印缺陷基本杜绝，产品的实物质量显著改善，客户的满意度明显提高。关键词：热轧带钢；表面辊印；分析；优化
中图分类号：TG335.5
文献标识码：B
doi:10. 13630/j. cnki. 13 1172.2017. 1117
文章编号：10065008(2017)11006502
ANALYSISINGANDIMPROVEMENTOF
SURFACEROLLERMARKSONTHEHOTROLLINGSTRIP
MaXiaochen，Liang Peng
(Technical Centre of Tangshan Delong Iron & Steel Co. Ltd., Tangshan, Hebei, 063604)
Abstract: The cause of roll marks on the hot strip steel surface of Tangshan Delong steel company is analyzed. According to the production situation, the roll marks on the strip steel surface are basically eliminated, the product quality has been improved significantly, and moreover the customer satisfaction has been significantly increased by optimizing heating temperature and rolling process, improving the cooling conditions of rolling, optimizing production scheduling, and strengthening the quality management of roller surface.
Key Words : hot rolling strip; surface roll marks; analysis; optimization
0
引言
随着制造业的快速发展，下游终端客户对原材料的质量要求越来越高。唐山德龙带钢厂生产线主要生产厚度为1.5~5.0mm、宽262~315mm带钢，钢种以碳素合金钢、低合金钢和优质碳素结构钢为主，产能120万t/a。与此同时，也产生了大量不合格品，其中以带钢表面辑印缺陷为主。由于辊印缺陷的存在，下游客户在冷轧过程中无法消除，造成深加工困难，既给客户造成经济损失，也有损德龙带钢产品的质量信誉。
为解决这一技术难题，公司技术人员总结了同
行业先进的生产经验，深人分析了表面辑印的产生原因，通过优化加热温度及轧制工艺、改善轧线的冷却条件、优化生产计划编排、加强轧辊表面质量管理
收稿日期：2017-08-01
作者简介：马啸晨（1992－），男，2014年毕业于河北理工大学轻工学院材料成型及控制工程专业，现在唐山市德龙钢铁有限公司技术中心.工.作,E mail:www. 420085611, com@ qq. com
万方数据
等措施，辑印缺陷基本杜绝，客户满意度明显提高，
1
辊印缺陷产生原因分析
所谓“辑印”缺陷是指钢板表面呈一定间距、周
期性分布、形状大小基本一致的局部凸凹缺陷，并且外观形状不规则1]，如图1所示。
图1表面辊印缺陷
Fig.1Surface defect of roller marks
带钢表面辊印缺陷直接取决于轧辊表面质量。利用停车换辊期间对所有平辊进行检查，发现精轧
65