总第250期 2016年第10期
河北治金 HEBEIMETALLURGY
小规格钢材氧氮分析方法的研究与应用
张育新
（河钢集团宣钢公司技术中心，河北宣化075100）
Total No. 250 2016,Number10
摘要：氧、氮元素是小规格钢材质量检验的重要指标，对其分析的即时性、准确性有更高的检测要求，尤其高尖端产品生产具有更重要意义。依据小规格钢材的特点，开发了钢材氧氮元素分析方法，该方法分
析速度快、结果准确率高、重复性好，已成功在实际工作中得到应用。关键调：小规格钢材；氧氮分析方法：研究；应用
中图分类号：TG115.3
文献标识码：A
doi;10. 13630/j. cnki. 13 1172.2016. 1006
文章编号：10065008(2016)100019-06
RESEARCHANDAPPLICATION
OFOXYGENANDNITROGENANALYSIS
METHODFORSTEELSWITHSMALLSPECIFICATION
Zhang Yuxin
( Technique Center, Hesteel Group Xuansteel Company, Xuanhua, Hebei, 075100)
Abstract: Oxygen and nitrogen elements are the important indexes in quality inspection for small specification steels, there is a higher demand for their analysis in instantaneity and accuracy, especially in high end prod ucts production. According to the characteristics of small specification steels, the analysis method for oxygen and nitrogen elements in steels is developed. It has features of fast, high accuracy and good repeatability, and has been used in actual work.
Key Words: small specification steels; oxygen and nitrogen analysis method; research; application
0
引言
当钢中氧含量过高时，会使钢的抗拉强度、届服
强度、冲击韧性及延伸率降低；当氮含量超过一定限，度时，易在钢中形成气泡，造成钢材组织疏松，韧性下降，脆性增加等缺陷。因此，氧、氮元素的检测是钢材质量检验的两个重要指标，对即时性、准确性有着更高的检测要求。在原有氧氮元素分析方法的基础上，利用现有分析仪器和制样设备，针对宣钢公司目前生产的钢种，研究了Φ6.5mm小规格钢材氧氮元素分析方法。
-
制备试样(")
Φ6.5mm以下棒状氧氮试样制样方法 1.1
GB/T11261-2006《钢铁氧含量的测定——脉冲加热情气熔融——红外线吸收法》和GB/T20124 收稿日期：201608-17
作者简介：张育新（1974－），男，高级工程师，1994年毕业于河北冶金工业学校机城专业，现在河集团宣钢公司技术中心从事质量管
理工作，Email:yangqian888999@ sina. com 万方数据
-2006《钢铁氮含量的测定—情性气体熔融热导法（常规方法）》中要求试样车制成Φ4~5mm圆棒。由于Φ6.5mm以下规格高碳硬线等钢材具有硬度高、直径小的特点，很难满足国标中对试样的车制制备要求。车制过程中存在刀头易损坏、制样周期长、试样表面易氧化等间题，增加了Φ6.5mm以下小规格钢材氧氮元素的检测难度。目前，氧氮元素日常检测采取“磨制-切块"常规加工方法。由于这种试样制备方法人为因素对加工效果影响较大，如果试样加工后表面粗糙、光洁度达不到规定要求，对后续的氧氮含量测定有不利影响，这种方法已不能满足日常分析需要。
经过大量试验探索，对小规格棒状试样采用“去氧化铁皮→一次表面抛光→二次表面抛光→切样→超声清洗→热风吹干→待测”制备工艺，并制定了小规格棒状试样的制备流程，如图1所示。
19