第32卷第6期
有色冶金设计与研究
提高韶冶烧结小矿山矿处理能力的研究与应用
戴孟良
（中金岭南韶关冶炼厂，广东韶关512024）
2011年 12月
【摘要]以韶关冶炼厂为例，详细分析了提高小矿山矿处理量对烧结工艺的影响，探讨了相关的设备技术改造和相应的稳定工艺措施，研究结果和生产实践表明其在降低生产成本方面具有明显效果和推广应用价值。
【关键词]烧结；小矿山矿；处理能力
中图分类号：TF046.4
文献标识码：B
文章编号：1004-4345(2011)060017-03
ApplicationandResearchofRaisingtheProportion
ofSmallMinesConcentrateinSinteringRawMaterialofShaoguanSmelter
DAI Meng-liang
(Shaoguan Smelter, Zhongjin Lingnan Nonfemet Company Limited, Shaoguan, Guangdong512024,China)
Abstract Taking Shaoguan smelter as an example, the paper analyzes the effect of raising the proportion of concentrate from small mines in raw material on sintering process, and discusses technical renovation and equipment upgrading as well as measures of stabilizing operation, The result and production practice show that raising the proportion of small mines concentrate in raw material has obvious effect in reducing operating cost and are worth popularization
Keywords sintering; concentrate from small mines; processing capacity
0前言
韶冶采用ISP工艺冶炼铅锌，目前具有两套相同的生产系统（I系统和Ⅱ系统）,其首要工序是烧结焙烧。其过程是各类硫化精矿(铅矿、锌矿以及铅锌混合矿)、返粉、各类冶炼中间物料(烟灰、电尘、废渣、粗氧化锌等）、钙质熔剂等按一定比例混合后通过圆筒制粒机完成制粒，生成具有一定强度的球状颗粒后进人烧结机。通过点火和鼓风烧结，上述物料发生一系列复杂的物理化学变化后生成具有一定强度和硬度的烧结块供鼓风炉熔炼，含SO，烟气经过收尘、净化后用于制酸系统I-2)。
2008年全球金融危机爆发，国际、国内有色金属生产企业受到较大冲击，面对严峻的经济形势，调整、优化烧结的原料结构，努力从源头上降低工厂生产成本成为必然选择。降低原料成本的有效措施之
收稿日期：2011-08-26
作者简介：戴孟良(1977-)，男，工程师，主要从事冶炼技术管理工.作。
一就是提高原料中价格相对低廉的小矿山矿比例，在烧结产能基本不变的前提下，可以减少价格较高的优质矿(凡口矿与进口矿）消耗量，从而达到调整、优化原料结构，降低成本的目的，这对于工厂来说无疑是一条切实可行的途径。
研究内容
1.1提高小矿山矿处理量对烧结工艺的影响 1.1.1对烧结制粒过程的影响
研究表明，与优质矿相比，小矿山矿的制粒性能较差，其原因主要是粒度偏粗，通过粒度测试得出的两类矿种大致粒级分布情况如表1所示。
表1韶冶小矿山矿与优质矿种大致粒级分布比较
数小矿山矿优质矿
<40 1.03 0.65
%
40~100 100~160 160220 220280>280
3.43 1.34
20.15 5.38
28.66 11.88
25.56 22.40
21.17 59.00
由上表可知，从两类矿种粒级分布来看大于或