宽厚板连铸坏角部
表面横裂纹成因及改进措施
吴伟勤
（南京钢铁股份有限公司板材事业部，江苏南京210035）
Total No.252 2016,Number12
摘要：铸坏边角部表面横裂纹是比较常见的表面缺陷之一，对铸坏的生产和质量影响很大。结合南钢公司一炼钢厂3#板坏连铸机铸坏实际生产和实物质量，分析了铸还在连铸机内的应力状态，筛选了影响板坏角部横裂纹的设备因素与工艺因素。通过改进设备和优化工艺，有效地控制了连铸坏边角部表面
0 关键词：宽厚板；连铸坏；角部表面横裂纹；成因；措施
中图分类号：TF777.1
文献标识码：B
doi;10.13630/j.cnki.13 1172.2016.1210
文章编号：10065008(2016)12003807
REASONANDIMPROVINGMEASURES
FORHORIZONTALCRACKSONCORNERSURFACE
OFCONTINUOUSCASTINGWIDEANDTHICKSTEELSLAB
WuWeiqin
(Plate Department, Nanjing Iron and Steel Co., Lid, Nanjing, Jiangsu, 210035)
Abstract : The horizontal crack on the edge corner surface is one of the normal surface defects of casting bil-let, and has a great influence on the output and quality of billet. Based on the practical production and prod uct quality of the slab of No. 3 caster in Nan Steel, the stress status of casting billet in the caster is analyzed the factors in equipment and process to affect the cracks are screened out. With improvement in equipment and process, the defect is effectively controlled, the defect rate of wide and thick plate in rolling is gradually reduced from 3.39% to below 0.5%
Key Words: wide and thick plate; continuous casting billet; horizontal crack on corner surface; cause; meas-san
引言
2014年初，南钢公司一炼钢厂3#板坏连铸机生
产宽厚板铸坏时常出现边角部表面横裂纹，未经清理的板坏轧制后宽厚板边部存在大量裂纹缺陷，成为影响钢板质量的一个重要因素。经对铸坏边角部吹扫检查，可看到铸坏边角部存在表面横裂纹。为改进铸坏边角部表面横裂纹缺陷，对板坏在连铸机内的应力状态进行分析，采取了相应的设备改进和
工艺优化措施，效果显著。收稿日期：2016-11-04
作者简介：吴伟勤（1980－），男，工程师，2001年毕业于重庆科技学院冶金工程专业，现在南京钢铁股份有限公司板材事业部技术研发
处从事工艺技术研发工作，Email；wuveiqin@njsteel,com.en 38
万方数据
连铸机主要参数
南钢公司一炼钢厂3#板坏连铸机主要设备参数见表1。
表1
Tab.1
项目设计公司铸机类型铸资数量钢包容量中间包容量铸机强半径
3#板还连铸机的主要技术参数
Main technical parameters of slab caster 3
技术指标 Siemens -VAI 直强型单机单流 155 t 40 t 10 m
项目铸机长度结晶器长度垂直段长度冷坏厚度冷坏宽度引铵杆系统
技术指标 32.115m 900mm 2.195m 220/260/320 mm 16002800mm
下装