原料缺陷致冷轧断带原因分析
李润昌，李欢，齐达
（首钢京唐钢铁联合有限公司，河北唐山063200）
Total No. 263 2017,Numberl1
摘要：介绍了表面有缺陷的热轧卷板在冷轧过程中产生的断带缺陷的形貌。分析对比了钢种基体与缺陷处的化学成分，认为导致冷轧断带的原因有两种：一是炼钢工序卷入的保护渣，二是热轧工序压人的
氧化铁皮。同时分析了裂纹扩展机理。关键词：冷轧；断带；保护渣；氧化铁皮
中图分类号：TG335.1
文献标识码A
doi: 1013630/j. cnki.13 1172.2017.1106
文章编号：10065008(2017)11002204
CAUSEANALYSISOFSTRIPBREAKAGEDURING
COLDROLLINGCAUSEDBYRAWMATERIALDEEEC
LiRnchang,LiHuan,QiDa
(Shougang Jingtang Iron and Steel Co. Ltd., Tangshan, Hebei, 063200)
Abstract : The hot rolled coil wit surface defects will break during cold rolli ng. By analyzing and comparing the chemical composition of the steel matrixand the defect, it is considered that there ar e two reasons for the strip breakage during cold rolling: one is the protectie slag involved in the steelmaking process, a nd the other is the oxide scale pressed into the hot rolling process. The mechnism of crack propagation is analyzed, too
Key Words: cold rolling; strip breakage; protective slag; iron scale
0
引言
在钢铁市场整体低迷的情况下，下游用户为了
控制生产成本在增大冷轧压缩比的同时，采用不经中间退火直接大压下量轧至目标厚度的方式进行生产，压下率普温达到85%~95%，这对热轧卷板的冷加工性能提出了更高的要求。冷轧基料用于制造加工易成型、强度要求不高的部件，市场需求量极大（2]。随着生产量的增加，前道工序缺陷流至冷轧产线的风险也随之增大。原料存在缺陷易因受力不均导致裂纹产生，裂纹在轧制过程中扩展易造成轧机处断带，严重影响冷轧工序生产节奏。且处理断带过程繁，给企业带来严重的经济损失。而对于
收稿日期；2017-08-07
作者简介：李润吕（1991－），男，助理工程师，2015年毕业于东北大学材料科学与工程专业，现在首钢京唐钢铁联合有限责任公司从事产品开发及过程质量控制，E-mail：liruichang12138@163.com
22
万方数据
热轧原料缺陷和受力的差异，对冷软过程中因轧制边裂而导致断带的影响，很难被发觉，且在此之前、很少有相关文献资料3-7
本文对冷轧轧制过程中，断带处存在的缺陷，裂纹发生原因和扩展机理进行了细致研究，并对缺陷形成原因进行了简要分析。
断带处缺陷形貌及成分分析
1
1.1缺陷宏观形貌
实验材料是从某冷轧产线轧制断带发生实例中获取的两种裂纹发生处缺陷样板，宏观形貌如图1 所示。