油基钻井液下水泥浆抗污剂的研究与应用
钟声
（中原石油工程有限公司固井公司，河南濮阳457001）
钟声.油基钻并液下水泥浆抗污剂的研究与应用[].钻并液与完并液，2016，33（5）：84-87
摘要针对目前油基钻井液下水泥易被污染，固井质量难以保证的间题，运用实验方法结合理论分析，开展了抗污染水泥浆体系的研究。利用人工岩心法证实了油基钻并液对固并质量有较大影响，特别是对二界面胶结强度影响最大。通过实验分析了基础水泥浆被油基钻井液污染后性能的变化，研制出了一种主要成分为烷基酚聚氧乙烯醚的抗污染剂Anti-P。室内实验结果表明，将1%抗污剂Anti-P加入水泥浆中，在水泥浆被少量油基钻井液污染后（小于10%)，水泥浆性能不受影响，保证了固井质量。将其在多口井进行应用，效果良好。该成果填补了目前抗污染水泥浆体系的空白，值得进一步研究推广。
关键词固井质量；水泥浆添加剂；抗污染；油基钻并液
中图分类号：TE256.6
文献标识码：A
文章编号：1001-5620（2016）05-0084-04
Study and Application of Anti-contamination Agent for Cement Slurry in Wells Drilled with Oil Base
DrillingFluids ZHONGSheng
(CementingBranch of Zhongyuan PetroleumEngineering Ltd.,Sinopec,Puyang,Henan 457001)
Abstract Wells drilled with oil base drlling fluid always have poor cementing job quality because of the contamination to the cement slurry by the oil base drilling fluid. Studies on the cement slurries that are resistant to contamination have been conducted using experimental method and theoretical analysis. In laboratory experiments with artificial cores, the effects of oil base drilling fluid on the cementing job quality, especially the effects of oil base drilling fluid to the bonding of the cement sheath and the borehole wall, have been proved. Anti-P (main component being alkylphenolpolyethoxylate), an anti-contamination agent for cement slurry was developed by studying the change of the properties of base cement slurry before and after being contaminated with oil base drilling fluid. Laboratory studies showed that cement slurry treated with Anti-P can stand the contamination by oil base drlling fluid of less than 10%, the properties of the cement slurry was not affected, and the cementing job quality satisfied the requirements. The application asnsaoeeeneossonanseaaaa worthfurther study and application.
Key words Well cementing job quality; Cement slurry additive; Anti-contamination; Oil base drilling fluid
油基钻井液的使用给固并带来很多困难。前人已对油基钻井液对固井质量的影响机理、前置液固井技术等进行了相关研究，并形成了相应的水泥浆体系。但还有较多困难需要克服，特别是目前关于抗油污染水泥浆研究还是一片空白，如何保证水泥浆在微量油基钻井液污染后的固井质量是垂需解决
的问题(-)。因此，笔者从油基钻并液固并难点着手，开展了抗油污染水泥浆体系实验研究。
1油基钻并液对二界面质量的影响
油基钻并液对固并质量的影响主要反映在对项替效率及第二界面胶结程度上，笔者采用人工岩心