文章编号：10062971(2012)040047-03
氮循环压缩机填料泄漏原因分析及解决措施周萍"，徐慧芬1，郑明芳，胡伟强2，许海平
（1.浙江江山化工股份有限公司，浙江江山324100；2.台州环天机械有限公司，浙江玉环317608）
故障分析
摘要：通过对循环机填料泄漏原因分新，找出因进口带液和冷却不良造成高温高压下填充聚四氯乙炜填料密封图冷流失效，提出解决措施。
关键调：氨循环压缩机：填料泄漏；材质和结构改造
中图分类号：TH475
文献标志码：B
Reason Analysis of Packing Leakage in,Ammonia Recycles Compressor and Solving Mea-sures
ZHOU Ping',XU Hui-fen',ZHENG Ming-fang",HU Wei-qiang°,XU Hai-ping
(1.Zhejiang Jianshan Chemical Co., Lid.Jiangshan 324100, China;2.Taizhou Huantian Machinery Co.Lid., Yuhuan 317608, China)
Abstract: Based on analyzing the reason of packing leakage in recycle compressor,it is found that it is due to the inlet with liquid and poor cooling to cause filling PTFE packing seal ring cold-flow failure under high temperature and pressure conditions-And the solving measures are pointed out.
Key words; ammonia recyeles compressor; packing leakage ; material and structural transformation
1引信言
DZW-4/280-314氨循环机是我公司氨醇系统的关键设备，该压缩机为单级、对置、双缸，双作用活塞压缩机，活塞杆是不贯穿的，轴端装有填料两密封，其冷却采用液氨，且采用无油润滑。
2主要的性能参数
进气压力(表压)：28MPa 排气压力（表压）：31.4MPa 排气量（吸人状态）：4m'/min
转速：282r/min 电机功率：355kW
润滑及冷却方式：传动机构为齿轮油泵供油润滑，气缸为无油润滑，填料为液氨冷却。
传动方式：三角皮带传动
收稿日期：2012-05~02
翼2012年04期（总第234期）
3填料泄漏情况
该机由上海嘉定机械厂制造，填料密封圈材质为填充聚四氟乙烯，自2003年1月投用后填料使用情况一直不好，活塞杆磨损也较严重，经常更换。据统计，填料使用寿命最短半个月左右，一般情况一个半月左右，同时因填料泄漏对活塞杆的冲剧磨损也较为严重，对安全生产造成了极大的影响。对该机在2005年至2011年因填料泄漏引起的故障情况进行统计，具体见表1。
原因分析 4
该机原填料密封圈材质为填充聚四氟乙烯，原结构用一个整环加盖的密封结构和一个整环开一个切口结构（见图1）。填充聚四氟乙烯在压力高时，易发生冷流变形。原填料发生泄漏时，拆检情况分析都有一个相同点，每组密封圈内圈均有挤出，也就是填充聚四氟乙烯密封圈在高温高压下冷流失效所致。为扭转这种十分不利的状况，
cm质机技水47