2014年第12期（总第111期）环境资源
经源与节社 ENERGY AND ENERGY CONSERVATION
制革污泥吸附电镀废水中Cr(VI)的研究
周玲玲，顾巧浓
（余姚市环境保护局，浙江余姚315400)
2014年12月
摘要：通过实验研完探索制革污泥吸附Cr（V)最佳的条件和工艺，提高电镀度水净化处理效果，既可解决制革污泥处理难的问题，实现废物资源化，又可降低处理电镀度水的成本，减轻环境压力。实验发现，随着C浓度增加，污混
吸附量也随着增加；污泥吸附的最佳pH值为3；最佳的据荡时间为30min；旧污泥与新污况相比有更好的吸附性。关键词：制革污泥；吸附；Cr(VI)；电镀废水
中图分类号：X5
文献标识码：A
文章编号：20950802(2014)12009602
Experimnental Study on Adsorption of Cr (VI) in Electroplating Wastewater with Tannery Sludge
ZHOU Lingling, GU Qiao-nong
(Yuyao Environmental Protectlon Bureau, Yuyao 3154oo, zhejlang, China)
Abstract: In order to explore the best conditions and techniques, and increase the chromium contaminated wastewater purificatlon effect, the adsorption of Cr (VI; onto tannery sludge has been investigated. It can solve the tannery sludge treatment problem, realize waste utllzatlon of resources, and can also Lower the treatment coats ot chromiumcontaminated wastewater. It ea aea eeoe s gee see se
and the best shaking time Is 30 min; the old sludge ls of better adsorbability than the new sludge. Key words: tannery sludge; absorption; Cr(Vi; electroplating wastewater
引言 0
浙江省各地都有电镀企业，电镀废水中含高浓度的Cu2*、Zn*、Pb*、Cr*、Cr、CN-离子，由于治理难度较大，电镀废水排放已造成水体严重污染。与此同时，温州制革业由于污泥和废水污染严重，也面临同样局面。本研究拟将制革污泥改性成吸附剂用于处理电镀企业无机废水，利用制革污泥自身所含大量有机质与废水中重金属离子发生整合反应从而达到净化污水和富集污水中重金属离子的目的，为电镀废水处理、制革污泥利用寻找双赢出路。
1
实验部分
实验材料 1.1
制革污泥取自于温州平阳。污泥中有害金属成分主要是Pb和Cr，浓度分别是0.6143mg/L和0.912 mg/L，除此之外，Al、Ca、S、P等含量也很高，浓度分别是89.385mg/L、51.81mg/L、67.26mg/L和16.71 mg/L。
收稿日期：2014-09-05
第一作者简介：周玲玲，1984年生，女，浙江余姚人，2007年
毕业于河北理工大学环境工程专业，工程师。· 96 ·
1.2实验方法
采用HNO-HSO消解法对样品进行预处理。称取 1g预处理后的污泥置于锥型瓶中，加人一定浓度Cr 标准溶液，在恒温培养摇床中振荡一定时间后抽滤，取适量滤液，用二苯碳酰二肼分光光度法测定。最终确定制革污泥吸附Cr(VI)最佳的pH值、振荡时间、污染溶液中Cr浓度，以提高对电镀废水的净化处理效果。
2
结果与讨论
2.1pH值对吸附量的影响
250
量/（ 100
o 吸
05
0
2
4
6 pH值
8
图1pH值变化对吸附的影响
10
12
由图1可知，pH值越小，制革污泥对Cr的吸附量越大，pH值越大对Cr的吸附量越小。当pH为3时，制革污泥吸附量最大，为197.16mg/L；当pH值为11时，