高镁粉替代白云石粉烧结实验研究
曹继礼，毛友庄，张惠，高振（山钢集团莱芜分公司，山东菜芜271104）
Sum.206 Oetober 2015
摘要：为提高烧结矿产质量，降低固体燃耗，采用工业实验的方法进行了高镁粉替代白云石粉可行性研究.结果表明：在莱芜分公司炼铁厂的原料工艺条件下，高镁粉可以作为镁质熔熔剂替代白云石粉，但是烧结矿产质量未达
到预期目标，熔剂成本升高太多，使用高镁粉取代白云石粉不经济关键调：烧结；高镁粉；白云石粉；实验
中图分类号：TF513
文献标识码：B
StudyonIndustrialSinteringExperimentofFineDolomite
Substituted by High-grade Fine Magnesia
CAO Ji li, MAO You -zhuang, ZHANG Hui, GAO Zhen
(Laiwu Branch Ironworks ,Shandong Iron and Steel Co. , Lad. , Laiwu, 271104,P. R. China)
Abstract: In order to improve the sintering quality and quantity, and reduce the solid fuel consumption, the industrial ex-periment has been done by means of replacing fine dolomite with high grade fine magnesia as magnesia flux. The industri-al production results show that the fine high grade magnesia can be used as a sinter MgO solvent additive under the raw material process conditions in the Iron works of Laiwu Branch, but the sintering quality and quantity does not achieve the expecting target and the cost of solvent increases obviously, it is not economical for replacing fine dolomite with fine high grade magnesia.
Key words: sintering: fine high grade magnesia; fine dolomite; experiment
0
前言
山钢集团莱芜分公司炼铁厂老区共有4座
1000m级高炉，经过大修扩容后烧结矿产能不足，不得不倒运烧结矿供给高炉，为了提高配套的老区烧结矿产质量1]，减少倒运损失，降低烧结矿固体燃耗2]，采用工业实验的方法进行了高镁粉替代白云石粉可行性研究，
1原料化学成分
白云石粉和石灰石粉为莱芜分公司炼铁厂长期使用的熔剂，化学性质稳定.本次工业实验所用的熔
剂化学成分平均值见表1. 收稿日期：20150520
名称白云石高镁粉石灰石粉
2
表1熔剂化学成分平均值
Sio, 4.16 3.86 2.51
实验方案
Cao 29.99 1.52 49.81
Mgo 19.73 83.61 2.88
1e/% H,o 1.11 0.47 1.02
本次实验共进行了两个阶段，第一个阶段为其
它熔剂种类不变的情况下，高镁粉直接替代白云石粉，增加白灰配比来调节碱度；第二阶段增加石灰石粉配比，高镁粉替代白云石粉，白灰配比小幅调整 2.1第一阶段
本阶段高镁粉共实验A堆B堆两个料堆，基准期为半堆生产，使用日常生产熔剂结构，实验期为另
作者简介：曹继礼（1984-），男，2008年毕业于安徽工业大学冶金工程，工程师，