30mm以上规格低合金钢板矫直工艺浅析与应用
李存林，戴文笠，巫献华，张唤唤
（宝钢集团广东韶关钢铁有限公司，广东韶关512123）
摘要：针对韶钢3450mm中厚板生产线30mm以上规格低合金钢板矫直弯曲率偏高间题，对现有的矫直设备能力及工艺参数进行了分析，并对矫直力和矫直扭矩进行了校核，确定了对30mm以上规格低合金钢板实施大压下
量矫直技术，并优化了矫直工艺，通过现场实施，矫直弯曲率大幅度降低，关键词：低合金钢板；压下量；挠度；矫直力
中图分类号：TG335.5*2
文献标识码：B
AnalysisandApplicationofLevelingProcessforLowAlloy
SteelPlatewiththeThicknessover30mm LI Cun lin, DAI Wen li, WU Xian hua, ZHANG Huan huan
( Plate Rolling Mill, Baosteel Group Shaoguan Iron and Steel Co. ,Ltd. ,Shaoguan ,Guangdong ,512123,P. R. China) Abstract: According to the problem of high leveling bending ratio for the low alloy steel plates with the thickness above 30 mm by SGIS 345Omm plate rolling line, an analysis on the leveling equipment capacity and process was carried out and the leveling force and the leveling torque were checked in order to detemine the higher reduction leveling technology for the low alloy steel plates with the thickness above 30 mm. By optimizing the leveling process and taking the countermeasures on site, the leveling bending ratio has been greatly reduced.
Key words: Low alloy steel plate; reduction; deflection; leveling force
0前言
宝钢集团广东韶关钢铁有限公司（以下简称“韶钢")3450mm中厚板生产线于2005年建成投产，年产能150万t，是一条具有国际先进水平的板材生产线.矫直机作为生产线的重要设备，决定着钢板的最终平直精度.2014年在矫直30mm以上规格低合金系列钢板时，矫直弯曲率一直居高不下，超过 6%，既影响了产品交货期，降低了生产效率，重新补轧也增加了生产成本.因此，很有必要对30mm以
上规格低合金钢板的矫直工艺进行优化 1
矫直机工艺状况分析 1.1矫直设备工艺布置分析
韶钢3450mm中厚板生产线热矫直机布置在收稿日期：2014-12-23
超快冷设备后，距离四辑可逆式轧机138m，离超快冷设备53m，热矫直机示意见图1.因30mm以上规格低合金系列钢板终轧温度800~850℃，终冷温度620~700℃，钢板的原始板型曲率不均匀；矫直机与轧机距离较远造成钢板矫直温度低，钢板矫直困难，弯曲率高，不平度超标，最终导致钢板的改判量增加